炉渣的岩相研究在转炉炼钢中的应用参考.docVIP

炉渣的岩相研究在转炉炼钢中的应用 摘要：岩相检验方法可以确定炉渣的矿相组成和分布。把岩相检验与炉渣化学成分、流动温度数据结合起来，可以更全面地了解炉渣的性质。本文介绍了不同成分铁水炼钢和溅渣护炉中的炉渣岩相检验结果和特点。 关键词：转炉炼钢 炉渣 结晶 岩相检验 Application of Mineralogical Morphology in Converter Steelmaking Yang wenyuan1 Wang Minglin1 Zou Jiezhong2 Cui Shuxian1 1.Central Iron and Steel Research Institute 2.Ping Xiang Iron and Steel Company Abstract: Composition and distribution of slag can be determined through mineralogical morphology inspection. Combined mineralogical morphology inspection and composition, fluid temperature of slag will display the characteristics of slag thoroughly. Composition and mineralogical characteristics of slag during steelmaking with different hot metal and slag splashing to protecting converter were studied. Key words: converter steelmaking; slag; crystal; mineralogical morphology inspection 1．前言 用岩相检验方法可以了解炉渣的矿相组成和分布。炉渣的矿相组成与炉渣的化学成分有密切关系。根据岩相检验结果可以判断炼钢过程的成渣情况。从生产现场取渣样时，其凝固速度都很快，岩相检验中所观察到的矿相及其分布与液体渣的结构很接近。炉渣的矿相晶体形状和分布与炉渣的过热度也有关系。把炉渣岩相检验结果与炉渣化学分析、熔点测定、炉渣的相图知识结合起来可以更全面地认识炉渣的性质。 钢铁研究总院在进行转炉高效吹氧、复合吹炼、不同成分铁水炼钢（正常含硅铁水、低硅铁水、中磷铁水、高磷铁水）、转炉溅渣护炉等多项研究中都应用岩相检验方法，并取得了良好效果。本文将对这些研究工作进行介绍。 2．正常铁水吹炼过程炉渣的岩相检验 正常铁水通常指铁水Si=0.4~0.6%，P0.012%，其它合金元素（V、Ti、Cr）不高的铁水。大多数转炉都用这种成份的铁水炼钢，其成渣过程和岩相组成也具有代表性。在宝山钢铁公司第一炼钢厂的300吨转炉利用副枪每隔3min左右取一次渣样、钢样并测温。所取试样都进行化学分析，炉渣进行岩相检验和熔点测定[1]。 表1 吹炼过程炉渣岩相组成的变化 Table 1 Composition of slag during different blowing satges 序号 吹氧时间/% R 橄榄石 镁硅钙石 C2S C3S RO MgO C2F 1 20 0.92 90 10 2 40 1.43 80 5 10 3 60 1.80 10 40 40 8~10 4 75 2.4 35 40 15 5 100 3.02 45 30 15 5 3 吹氧量达到20%，炉渣主要矿相是粗大的柱状晶体绿色钙镁橄榄石CaO·(Mg,Fe,Mn)O·SiO2，占总矿相的90%，中间充填少量RO相（1a）。随着吹炼的进行，炉渣矿相出现少量镁硅钙石（3CaO·MgO·SiO2），炉渣主要矿相仍为酸性的橄榄石（1b）。当吹氧量达到60%时，炉渣碱度1.8，渣中主要矿相为黑褐色粒状硅酸二钙（2CaO·SiO2）和浅绿色隐条状的镁硅钙石，两者各占总矿相量的40%。低熔点橄榄石和RO相各占10%，充填在晶界上（1c）。随着吹炼的进行，渣中低碱度矿相消失，高碱度矿相量增加，到吹炼终点时渣中主要矿相是兰色粒状硅酸三钙（3CaO·SiO2）和褐色粒状硅酸二钙，两者各占30%和45%，RO相与未熔MgO两者之和约20%，并有少量铁酸钙（2CaO·FeO）（1e）。1（f）是渣中被硅酸二钙壳所包裹的未熔石灰照片。从岩相照片看宝钢一炼钢转炉化渣情况是比较好的，炉渣各矿相的分布均匀。渣中的硅酸三钙相有30~40%，硅酸三钙有较强的脱磷能力。渣中有15~20%的RO相和铁酸钙相，这些低熔点矿相使