Accepted Manuscript Corrosion performance of medical grade NiTi after laser processing A. Michael, A. Pequegnat, J. Wang, Y.N. Zhou, M.I. Khan PII: S0257-8972(17)30582-0 DOI: doi: 10.1016/j.surfcoat.2017.05.092 Reference: SCT 22411 To appear in: Surface Coatings Technology Received date: 22 March 2017 Revised date: 30 May 2017 Accepted date: 31 May 2017 Please cite this article as: A. Michael, A. Pequegnat, J. Wang, Y.N. Zhou, M.I. Khan , Corrosion performance of medical grade NiTi after laser processing, Surface Coatings Technology (2017), doi: 10.1016/j.surfcoat.2017.05.092 This is a PDF file of an unedited manuscript that has been accepted for publication. As a service to our customers we are providing this early version of the manuscript. The manuscript will undergo copyediting, typesetting, and review of the resulting proof before it is published in its final form. Please note that during the production process errors may be discovered which could affect the content, and all legal disclaimers that apply to the journal pertain. ACCEPTED MANUSCRIPT Corrosion Performance of Medical Grade NiTi after Laser Processing 1 1 1 1 2 T A. Michael *, A. Pequegnat , J. Wang , Y.N. Zhou , M. I. Khan P I 1Centre for Advanced Materials Joining (CAMJ), Department of Mechanical and Mechatronics R Engineering, University of Waterloo, 200 University Avenue West, Waterloo, ON, Canada N2L C 3G1 S 2 U Smarter Alloys Inc., 75 Bathurst Drive, Waterloo, Ontario, N2V1N2 N