焊接激光工艺外文文献.pdfVIP

Journal of Manufacturing Processes 30 (2017) 83–96 Contents lists available at ScienceDirect Journal of Manufacturing Processes j o u r na l h o me p a ge : w w w. elsev /locate/manpro Technical Paper Effect of welding laser process on macrostructures and the mechanical properties of coating steel DP600: Influence of vaporization zinc A. Kouadri-Henni ∗,1 European University of Brittany, INSA, LGCGM, EA 3913, 20 Avenue des Buttes des Coesmes, F-35708 Rennes, France a r t i c l e i n f o a b s t r a c t Article history: This paper presents an analysis of the shear strength evolution of laser welds. DP600 steel sheets, with Received 16 January 2017 a thin zinc coating, were welded in a lap joint configuration. With the aim of optimisation, it has been Received in revised form 2 July 2017 shown that the mechanical set up, i.e. weld gap and clamping force associated with speed and laser Accepted 24 July 2017 power, permit a significant increase in mechanical properties notably in shear strength when the zinc Available online 20 September 2017 vaporization is optimized. This amelioration required a negative defocusing (−0.33 mm) and a minimal weld gap (0.2 mm) to allow zinc vapour to escape the weld pool and thus av