CrMoN太阳能选择性吸收涂层.pdf

Solar Energy Materials Solar Cells 109 (2013) 97–103 Contents lists available at SciVerse ScienceDirect Solar Energy Materials Solar Cells journal homepage: /locate/solmat Spectrally selective CrMoN/CrON tandem absorber for mid-temperature solar thermal applications N. Selvakumar a, S. Santhoshkumar a, S. Basu b, A. Biswas b, Harish C. Barshilia a,n a Surface Engineering Division, National Aerospace Laboratories (CSIR), Bangalore 560017, India b Applied Spectroscopy Division, Bhabha Atomic Research Center, Mumbai 400085, India a r t i c l e i n f o a b s t r a c t Article history: CrMoN(H)/CrMoN(L)/CrON tandem absorber was deposited on stainless steel (SS) and aluminum (Al) Received 9 April 2012 substrates by the sputtering method. The nitrogen flow rate was varied in order to obtain the CrMoN(H) Received in revised form (high metal content) and CrMoN(L) (low metal content) layers. The structural properties of the coatings 5 October 2012 were studied using the X-ray diffraction technique. The optimized tandem absorber on SS substrate Accepted 7 October 2012 exhibited high absorptance in the range of 0.90–0.92 and emittance in the range of 0.13–0.15. The optical constants of CrMoN(H), CrMoN(L) and CrON layers were obtained from spectroscopic ellipso- Keywords: metric measurements. The optical constants data revealed that the CrMoN(H) layer is the main Chr