S2钢种缩小供料尺寸制程改善-中国矿冶工程学会互动式网站.PDFVIP

S2鋼種縮小供料尺寸製程改善 The Process Improvement of Reduce S2 Steel Supply Size 1 2 2 C.M. Kuo, S.L. Liang , Y.Y. Lin In the past, the coil that to be produced into bit is imported from Europe and Japan. The price is very expensive and unstable supply. In order to help 85 the domestic hand tool manufacturers to cost down S2 S2- and improve international competitiveness, CSC 1M2 S2-1M3 developed S2 steel in 1996, and gradually developed a higher grade S2- 1M2 and S2- 1M3 steel. But the 8mm rod size is still 8mm above. It needs to go through several drawn, spheroidizing annealing and other processing procedures before making the finished product. 99 To meet cu stomer demand, the CSC Rod 2 Mill began commissioning in 20 10. The rod could 5.5~7mm S2 be rolled with low temperature controlled rolling. Finally b e able to produce 5.5~7mm small size S2 steel. Customers could reduce several drawn, sph er oidizin g ann ealin g an d oth er pr ocessin g process. To shorten delivery time, cost down, stable quality, energy conservation carbon reduction. 關鍵詞：S2 Key words: CSC #2 Rod Mill, S2 steel 一、前　　言 S2 8~32mm S2 DI 5.5~7mm (1) (2) 1 2 鑛冶 58/1 －103 － 二、中鋼線材二場概述