PP改性效果评价刘志敏（烟台大学化学院，专业：高分子材料与工程，学号：201055507230）摘要：聚丙烯是一种性能优良的塑料，它的耐腐蚀性、耐折叠性和电绝缘性好，耐热性和机械强度由于聚乙烯，而且价格低廉，容易加工。但是聚丙烯的抗冲击强度不够高，低温下发脆，容易燃烧。为了提高它的韧性，常常将聚丙烯和橡胶弹性体共混改善提高它的韧性；对其进行阻燃改性最常用的方法是把无机阻燃剂填充到聚合物基体中赋予聚合物以阻燃性。添加的助剂有：聚烯烃弹性体、氢氧化镁、抗氧剂1010、偶联剂、硬脂酸等助剂。经过试验测得添加助剂后的材料在抗冲击强度、硬度、氧指数等方面都有明显的改善。关键词：聚丙烯、 改性剂 、 阻燃剂Abstract：Polypropylene is a kind of high performance plastic, its corrosion resistance, folding resistance and good electrical insulation, heat resistance and mechanical strength because of polyethylene and the price is low, easy to processing.But the impact strength of PP is not high, low temperature issued crisp, easy to burn.In order to improve its toughness, often to polypropylene and rubber elastomers blending to improve its toughness;On the flame retardant modification of the most commonly used method is to fill the inorganic flame retardant in the polymer matrix polymer with flame retardancy.Adding additives: polyolefin elastomeric, magnesium hydroxide, antioxidant 1010, coupling agent and stearic acid additives.After adding additives measured in experiment, the materials in the impact strength, hardness and oxygen index have been improved obviously.Keyword: Polypropylene、 Modifier 、 Flame retardant 前言聚丙烯是一种应用非常广泛的塑料，而且性能优良，但是有一些不足之处，如低温下发脆，容易燃烧等缺点。因此，针对聚丙烯的这些不足进行改性，以提高材料的使用价值。我们通过查阅书籍资料、网上搜索等途径，获得了聚丙烯的改性的配方，提高韧性的配方是：PP、POE、抗氧剂；阻燃的配方是：PP、氢氧化镁、抗氧剂、硬脂酸、三氧化二锑、偶联剂。通过改性的材料和设置的空白样进行对照，由实验数据可得出改性效果的好坏。PP改性的研究一、配方设计：通过查阅资料，并在老师的指导和帮助下，确定了PP改性的配方，如下图表：增韧改性配方（份数）：　A1B1C1A2B2C2POE0510152025抗氧剂0.50.50.50.50.50.5阻燃改性配方（份数）：　A3B3C3PP100100100Mg(OH)2 203040Sb2O31.51.51.5抗氧剂0.50.50.5硬脂酸0.50.50.5偶联剂0.50.50.5配方的设计是根据材料的不足而设计的，针对PP的低温脆性，选择POE橡胶弹性体和PP共混来提高它的韧性；对于阻燃，选择氢氧化镁无机阻燃剂添加到聚合物基体中赋予其阻燃性，是因为氢氧化镁在高温下通过分解吸收大量的热量，生成的水蒸气可以稀释空气中氧的浓度，从而缓解聚合物的热降解速度，减小火势抑制燃烧，促使炭化、抑制烟雾的形成等优点。偶联剂等其他助剂的加入都是为了增加物料和填料的配合性。二、操作过程：实验分成A、B、C三组，每组的配方总质量为：增韧配方：500g，阻燃配方：600g。称量所需的原料以及各助剂的量，按所占份数称量，重量大约为：A1组：PP：500g POE：0 抗氧剂：2.5gA2组：PP：420g POE：90g抗氧剂：2.5gA3组：PP：500g 氢氧化镁：100g 三氧化二锑：7