建筑节能测与评估实习总结.doc

实习总结 摘要：在这次实习试验中主要研究了蒸压加气混凝土砌体的轴心抗压强度，讨论蒸压加气混凝土砌体的裂缝发展特点和破坏特征及其影响因素．分析其抗压承载力、弹性模量及应力应变关系，并与传统砌体材料进行对比分析。结果表明蒸压加气混凝土砌体开裂后砌体还可以承受一定的压力，延性较好，蒸压加气混凝土承重砌块砌体的强度与传统承重砌体的强度水平相当． Abstract: in this practice test mainly studied in vapor axial compressive strength aerated concrete masonry, compressive factors discussed steamed aerated concrete masonry crack development characteristics and damage characteristics and its effect. The analysis of the compressive strength, elastic modulus and stress strain relation, and the results were compared with the traditional masonry materials. The results show that the autoclaved aerated concrete masonry cracking masonry can bear certain pressure, good ductility, strength level of autoclaved aerated concrete bearing masonry strength with the traditional bearing masonry. 关键词： 蒸压加气混凝土砌块 蒸压加气混凝土砌体 强度 弹性模量 传热系数 Key words: Autoclaved aerated concrete block Masonry of autoclaved aerated concrete masonry Strength Modulus of elasticity Heat transfer coefficient 一. 蒸压加气混凝土砌体的砌筑 蒸压加气混凝土砌块的单位体积重量是粘土砖的三分之一，保温性能是粘土砖的3-4倍，为了研究蒸压加气混凝土砌块的抗压，抗剪和保温性能，于是砌筑蒸压加气混凝土墙体进行试验。因为灰缝厚度对砌体的保温性能和抗压强度有影响，砌筑时灰缝要做到横平竖直，上下层十字错缝，转角处应相互咬槎，砂浆要饱满，水平灰缝不大于15mm，垂直灰缝不大于20mm，砂浆饱满度要求在90%以上，垂直缝宜用内外临时夹板灌缝，砌筑后应立即对墙体灰缝用原砂浆内外勾缝压实，以保证砂浆的饱满度及密实度。砌筑墙体时加气混凝土砌块的生产龄期应超过15天，不应使用破裂、不规整和表面被污染的加气混凝土砌块，严禁使用干砖或含水饱和的砖。在砌块墙底部应用小块实心水泥砖砌筑（或捣C10混凝土），其高度不宜小于200mm。 （墙体砌筑过程） （进行墙体养护） 二.蒸压加气混凝土砌块强度试验 （一）蒸压加气混凝土砌块强度试验目的及基本要求 蒸压加气混凝土砌块强度试验目的：测量单个蒸压加气混凝土砌块的强度 蒸压加气混凝土砌块强度试验中用到的相关材料、设备： 相关设备:材料试验机 千分表 材料：蒸压加气混凝土砌块 试件要求：（1）尺寸分别为98mm× 98mm×100mm，99mm×99mm×100mm，98mm×99mm×100mm立方体；（2）试件表面须平整，不得有裂缝或明显缺陷； （3）试件应沿制品发气方向中心部分按上、中、下顺序锯取，共取3组9块。 （二）试验的加载过程 试验加载过程： 1．测量试件尺寸精确至lmm，并计算试件的受力面积； 2．将试件放在试验机的下压板的中心位置，试件的受力方向垂直于制品的发气方向； 3．开动试验机，当上压板与试件接近时，调整球座，使接触均衡。以(2．0±0．5)kN／s的速度连续而均匀地加荷，直至试件破坏，记录破坏荷载值。 试验加载过程中注意问题： 1.如果试件尺寸精确度不一致，则计算的受力面积也可能不一致，最终导致计算的抗压强度偏大或偏小。 2.应严格控制加荷速率，因为加荷速率大时，破坏荷载值也大：相反，加荷速率小时，破坏荷载值也小。 三. 蒸压加气混凝土砌体抗压强度测试及弹性模量测试 （一）蒸压加气混凝土砌体强度试验的目