玻璃钢行业常用术语（Commonly used terms in glass fiber reinforced plastics industry）.docVIP

玻璃钢行业常用术语（Commonly used terms in glass fiber reinforced plastics industry） Plate Generally refers to the thickness of more than 2 millimeters of soft flat materials and thickness of more than 0.5 mm hard plane material. 3. translucency Translucence The object can only pass through a part of visible light, but it can not clearly observe the properties of other objects through it. 4. package Encapsulation A thermoplastic or thermosetting resin is applied to the workpiece by coating, dipping and spraying, and the outer surface of the resin is coated as a protective coating or an insulating coating. 5. film Film Generally refers to the thickness of 0.25 mm below the smooth and soft plastic products. 7. blasting strength Bursting strength Plastic containers, pipes, films, etc., can withstand the maximum pressure exerted continuously by liquid or air during blasting tests. 8. color change Discoloration The change of color of plastic products caused by light, heat, outdoor exposure and chemical reagent. 9. apparent density Apparent density The quality of test materials (including voids) per unit volume. 10. surface resistivity Surface treating agent The ratio between the potential gradient parallel to the current direction on the material surface and the current on the surface unit width is expressed in ohms. (Note: if the current is stable, the surface resistivity is numerically equal to the surface resistance between the two electrodes on both sides of the square material, and is independent of the square size.) 11. C - phase (C- stage) C-stage The last stage of some thermosetting resins in the ripening reaction. In this stage, The resin is neither dissolved nor melted. 12. ripple Waviness Wavy and uneven defects on the surface of plastic products. 13. unsaturated polyester Unsaturated polyester Polyesters containing unsaturated bonds on the molecular backbone. 18. differential thermal analysis (DTA) Differential thermal analysis A method of analyzing substances. When th