试论电厂施工建设中预防锅炉爆管和泄漏措施.docVIP

试论电厂施工建设中预防锅炉爆管和泄漏措施 　　摘要：电厂锅炉爆管和泄漏是指锅炉水冷壁、过热器、再热器和省煤器泄漏。锅炉四管爆管和泄漏故障是一个影响机组安全稳定运行的问题，我国火电机组由于炉管事故引起的非计划停运小时数占机组非计划停运总时长的37.8％，而美国仅为7％。因此分析四管泄漏的原因及找到对策是非常必要的。本文首先分析了电厂施工建设中锅炉爆管和泄漏的部位及原因，最后从五大方面详细探讨了电厂施工建设中预防锅炉爆管泄漏的措施。 　　关键词：电厂；锅炉爆管；四管泄漏；磨损；超温 　　Pick to: the power plant boiler tube leak and refers to the boiler water wall, superheater, reheater, and economizer leakage. Four tube boiler tube leak and failure is a problem affecting the safe and stable operation of unit, thermal power unit in China due to the accident of furnace tube caused by unplanned shutdown hours accounting for 37.8% of the units are not plan to stop the total, while the United States is only 7%. So the analysis of the causes for the leakage of tube and find countermeasures is very necessary. At first, this paper analyzes the construction of power plant boiler tube and leakage in the construction of the site and the reasons, finally in detail from five aspects discusses the power plant construction in the construction of the measures to prevent boiler tube leakage. 　　Key words: power plant; Boiler tube; Four pipe leakage; Wear and tear; overtemperature 　　中图分类号：TM621.8文献标识码：A文章编号：2095-2104(2013) 　　 　　电厂施工建设中锅炉爆管和泄漏的部位及原因分析 　　（一）水冷壁管泄漏 　　 　　图1水冷壁管爆管 　　在四管泄漏中，水冷壁管产生爆漏除设计、制造、安装的原因外，还与磨损、腐蚀、膨胀受阻、急冷、水循环不良等有关。 　　1、磨损 　　水冷壁管磨损主要发生在一次风喷口周围，是由风粉流冲刷和吹灰器吹扫时冲刷等引发的磨损。 　　在一次风喷口周围水冷壁管发生磨损时，主要是喷燃器安装角度不恰当、设计切圆过大、喷嘴在运行中烧坏变形以及稳燃设施布置不当等，使煤粉气流冲刷水冷壁管，引起管壁磨损变薄，以至泄漏。 　　2、腐蚀 　　（1）水冷壁管外壁高温腐蚀 　　水冷壁外壁高温腐蚀通常发生在高温高压锅炉热负荷高的区域，即喷燃器附近。 　　（2）水冷壁管内壁腐蚀 　　当水冷壁管内有沉积物（垢或水渣）时，在这些沉积物下面会引起水冷壁腐蚀，这种腐蚀称为酸、碱腐蚀。这是因为炉水中的酸性、碱性盐类破坏了金属保护膜的缘故。 　　膨胀受阻 　　水冷壁因膨胀受阻而拉裂的现象时有发生，拉裂部位通常在炉膛四角和喷燃器附近，多数是由于大滑板与水冷壁膨胀不一致，经多次启停炉后，就从焊点处拉裂泄漏。另外，膜式水冷壁锅炉两侧水冷壁与水平烟道过热器管排交接处密封板也是水冷壁膨胀受阻的部位。 　　（二）省煤器泄漏 　　 　　图2省煤器泄漏 　　1、省煤器磨损机理 　　由于流过锅炉受热面的烟气具有一定的速度，在烟气中又含有形状不规则的固体颗粒，这些颗粒流经受热面时，就会对受热面产生撞击和磨擦。磨损主要是由于灰粒对管壁撞击和磨削引起，磨损之所以多发生在冲击角为30°～50°的部位，那是由于烟气速度、飞灰浓度、粒度随时都在变化的结果。 　　省煤器易磨损的部位 　　省煤器的磨损，主要表现为局部磨损和均匀磨损两个方面，尤其是局部磨损易引起省煤器漏泄，其位置多发生在省煤器左右两组的中部弯头、靠近前后墙的几排管子、