ti-6al-4v与sic超声波钎焊界面形成机理及工艺研究-study on formation mechanism and process of ultrasonic brazing interface between ti - 6al - 4v and sic.docxVIP

在近钎缝的SiC陶瓷侧表面上，SiC陶瓷在该应力作用下发生断裂。通过在Al-Si基钎料中加入Sn和Zn两种元素降低了钎料的固相线，进而降低了残余应力开始产生的温度，获得了低应力的Ti-6Al-4V/SiC钎焊接头。关键词：钛合金；SiC陶瓷；空蚀效应；界面反应；超声波辅助钎焊AbstractSiliconcarbide(SiC)ceramicshavebroadapplicationprospectsinindustry,suchasmachine,aerospace,petroleum,nuclearenergy,opticsandotherfields,duetotheirgoodperformancesofstrongoxidationresistance,goodabrasionresistance,highhardness,goodthermalstability,lowcoefficientofthermalexpansion,highthermalconductivity,excellentthermalshockresistance,etal.Ti-6Al-4Vtitaniumalloyswithhighstrength,corrosionresistanceandotheroutstandingadvantagesarewidelyusedinaerospace,