LiFePO4电池空电态和满电态搁置性能研究.docVIP

LiFePO4电池空电态与满电态搁置性能研究江苏华富储能新技术发展有限公司 孙庆 沙树勇 代云飞 吴战宇 摘要：本文考察了LiFePO4电池（10Ah）单体在空电与满电态两种荷电态下搁置半年时的性能。实验结果表明：搁置后空电态样品并未出现预期可能出现的亏电现象，反而仍能放出电量，且可恢复容量还要高于搁置前容量；而满电态样品容量有所衰减，但最大衰减容量也仅为300mAh，其不可逆容量损失也不到200mAh。从剩余容量与不可逆容量看，空电态比满电态下搁置更有利。在20次的循环二种状态下搁置半年后的样品容量保持率相当，搁置后的循环性能还有待进一步验证。关键词：LiFePO4；自放电；搁置性能；SOC； 中图分类号：TM911Abstract: In this study, performance of the 10Ah lithium ion battery with LiFePO4 electrode was investigated after a half year of storage in the uncharged and fully charged states. The results indicated that no performance degradation occurred to the battery after the storage in the unc