无机盐li2co3复合bace0.7zr0.1y0.2o3-δ质子导体制备与改性研究-study on preparation and modification of inorganic salt li2co3 composite bace 0.7 zr 0.1 y 0.2 o 3 - δ proton conductor.docxVIP

下载本文档

22
0
约5.41万字
约 50页
2018-08-10 发布于上海
举报

无机盐li2co3复合bace0.7zr0.1y0.2o3-δ质子导体制备与改性研究-study on preparation and modification of inorganic salt li2co3 composite bace 0.7 zr 0.1 y 0.2 o 3 - δ proton conductor.docx

无机盐li2co3复合bace0.7zr0.1y0.2o3-δ质子导体制备与改性研究-study on preparation and modification of inorganic salt li2co3 composite bace 0.7 zr 0.1 y 0.2 o 3 - δ proton conductor

ABSTRACT This work was based on low-temperature proton conductor SOFCs. Effects of various amounts of Li2CO3 on sintering behavior, chemical stability and electrochemical properties of BaCe0.7Zr0.1Y0.2O3-δ (BCZY) were systematically investigated. BaCe0.7Zr0.1Y0.2O3-δ (BCZY) electrolyte materials were synthesized by a combustion method. XRD results showed that BCZY powders calcination temperature must be at 1000 ?C or above in order to obtain a single perovskite structure of oxide powder. BCZY powders which were synthesized by a combustion method had large surface area and high sintering activ

您可能关注的文档

文档评论（0）

1亿VIP精品文档

更多 >

无机盐li2co3复合bace0.7zr0.1y0.2o3-δ质子导体制备与改性研究-study on preparation and modification of inorganic salt li2co3 composite bace 0.7 zr 0.1 y 0.2 o 3 - δ proton conductor.docxVIP