三种泡沫沥青最佳发泡条件探讨.docVIP

三种泡沫沥青最佳发泡条件的探讨 　　【摘 要】本文通过对不同沥青发泡温度、不同发泡用水量下的沥青发泡特性(膨胀比和半衰期)来分析韩国SK70号、SK90号以及中海70号基质沥青三种泡沫沥青的最佳发泡条件,试验结果表明:三种沥青的发泡特性由高到低依次为中海70号、SK70号、SK90号。 　　【关键词】沥青路面;冷再生;泡沫沥青;发泡温度;发泡用水量 　　Three types of foam asphalt of the best foaming conditions 　　Wei Zhen-chen ??1, Wang Zhen-long??2 　　(1. Shandong Hengjian Project Management Consulting Co., Ltd. Weifang Shandong 261061; 2. Guangdong Shanjie Expressway Co., Ltd. Guangzhou Guangdong 515556) 　　【Abstract】Based on the different bitumen temperature under different water bitumen foaming characteristics (expansion ratio and half-life) to analyze Korea No. SK70, SK90, and No. 70 in the sea foam bitumen asphalt the best hair of three bubble conditions, test results showed that: the foam characteristics of asphalt in the sea in order were 70, SK70 number, SK90 number. 　　【Key words】Asphalt pavement; Cold regeneration; Foam asphalt; Foaming temperature; Foaming water 　　1. 前言 　　随着我国公路交通事业的蓬勃发展,大部分省份高速公路和国省道干线路网已经基本形成,而且许多公路陆续进入大修期。但是长期以来我国公路大修时存在方案设计单一,维修工艺较落后,施工成本高,社会效益差等弊病。因地制宜的选择合理、科学的现代化维修方案和工艺技术成为目前公路管理和养护部门的迫切要求。泡沫沥青冷再生技术近年在国外日渐兴起,并在各地得到广泛应用。这项技术是利用沥青发泡技术将废弃的路面铣刨材料重新再生利用,并在压实力的作用下形成具有一定路用性能的路面结构层。这项技术不仅可以将废弃的路面铣刨材料再生使用,而且沥青铣刨材料中的老化沥青可以重新激活,可以变废为宝,从而达到保护环境、节约资源的作用;同时利用泡沫沥青再生技术可以将传统的路面结构改造成柔性基层路面结构,从而优化路面组合形式,延长路面使用寿命。本文主要通过试验研究泡沫沥青的两个主要指标:膨胀比和半衰期,从而来确定韩国SK70号和中海70号基质沥青的最佳发泡条件。 　　2. 沥青发泡的试验材料及试验方法 　　2.1 试验材料和参数。 　　本次试验以常用的韩国SK70号和中海70号基质沥青为研究对象,有关三种基质沥青的相关技术指标见表.1所示。 　　2.2 试验方法。 　　本次试验采用德国维特根公司生产的WLB10型沥青发泡试验机进行。沥青发泡受多种因素的影响,如沥青的类型、沥青的温度、发泡加水量、发泡时的水压和气压,因此,试验前需要对各个环节进行仔细把握,沥青发泡的具体试验步骤如下: 　　(1)在无压的状态下向水槽中注水,将水槽和气槽的压力表调节至要求的压力。本次试验设置空气压力为5bars,水压力为6bars,水压一定要比空气压力高1bar。 　　(2)开启加热系统给沥青加热:将沥青注入到沥青槽中,并加热至所需温度,并应使发泡前沥青保持该温度约5分钟左右。此次选定四种沥青发泡温度150℃ 、160℃、170℃、180℃进行发泡试验。 　　(3)调整发泡所需的水量:根据沥青流量,分别选定用水量为1.5%、2.0%、2.5%、3.0%、3.5%来进行发泡。 　　(4)将生产出来的泡沫沥青用容积为20升的洁净的钢桶收集起来。量测泡沫沥青膨胀比和半衰期。 　　(5)试验结束后必须彻底清洁沥青循环管道,将沥青罐清理干净,以备下次试验使用。 　　2.3 试验结果。 　　韩国SK70号基质沥青和中海70号基质沥青在不同沥青发泡温度、不同发泡用水量下的沥青发泡特性试验结果如表2~3所示。 　　3. 沥青发泡特性分析 　　3.1 韩国SK70号