Zn2SnO4纳米材料的制备及性能研究（毕业学术论文设计）.docVIP

摘 要 通过比较多种不同的方法，以及借鉴其他物质的制备方法，决定采用聚合物前驱体法，这种方法目前还没有人用来制备Zn2SnO4纳米粉体。并利用X射线衍射、红外、比表面积等手段对制得的样品进行表征。鉴于Zn2SnO4纳米粉体的光催化性能及光致发光性能较好，于是对Zn2SnO4纳米粉体的光催化性能、光致发光性能进行测试。分析结果表明，制得的粉体为Zn2SnO4纳米粉体、SnO2和ZnO的混合粉体，混合粉体的光催化性能及光致发光性能均较好。 关键字：Zn2SnO4纳米粉体 聚合物前驱体法 光催化性能 光致发光性能 Abstract By comparing several different ways, and learn from other substances in preparation methods, decided to adopt the polymer precursor method which havent being used in preparing Zn2SnO4 nanometer powder. The samples obtained were characterized by means of XRD, IR, BET surface area. In view of the good performance of Zn2SnO4 nanometer powder, so decided to test the photocatalytic properties and photoluminescent properties of Zn2SnO4 nanometer powder. The results show that the obtained powder was the mixture of Zn2SnO4 nanometer powder, SnO2 and ZnO powder, and the Photocatalytic Property and photoluminescence properties of mixed powders are good. Keyword: Zn2SnO4 nanometer powder Polymeric Precursor Methods Photocatalytic Property Photoluminescence Property 目录TOC \o 1-3 \h \u 第一章 前言?????????????????????????????????????????????????????????????????????????????????????????????????1 1.1 Zn2SnO4纳米材料及其应用?????????????????????????????????????????????????????????????1 1.1.1 半导体材料?????????????????????????????????????????????????????????????????????????????????????1 1.1.2 气敏材料?????????????????????????????????????????????????????????????????????????????????????????1 1.1.3 电池负极材料??????????????????????????????????????????????????????????????????????????????????2 1.1.4 无机阻燃剂及阻燃涂料（ZnSnO3）???????????????????????????????????????????????????2 1.1.5 镁-锂合金表面防腐材料????????????????????????????????????????????????????????????????????3 1.2 Zn2SnO4纳米材料的研究现状及发展??????????????????????????????????????????????3 1.3 Zn2SnO4纳米材料的制备方法??????????????????????????????????????????????????????????4 1.3.1 水热合成法??????????????????????????????????????????????????????????????????????????????????????4 1.3.2 低温固相反应??????