《水热合成不同形态YF3纳米线及其表征》-毕业论文（设计）.doc

水热合成不同形态YF3纳米线及其表征 摘 要 本课题采用以NH4F为氟源，Y(NO3)3为钇源，在不同反应温度，不同PH值的条件下，通过简单的水热法合成了纳米粉体沉淀，经洗涤、过滤、干燥粉碎、真空脱水制得不同形态的氟化钇晶体，再经过X射线衍射(XRD)结果表明所得的产物确实为YF3晶体。用扫描电子显微镜(SEM)和透射电子显微镜(TEM)对产物的形貌表征，表明产物是纳米线结构 关键词：纳米线，水热合成，YF3 Room temperature, controlled synthesis of nanowires of different forms and Characterization YF3 ABSTRACT This topic used to NH4F as the fluoride source, Y (NO3) 3 as the yttrium source, at different reaction temperatures, under conditions of different PH values, by a simple hydrothermal synthesis of nano powder precipitation, washing, filtration, dried and crushed vacuum dehydration of various forms of yttrium fluoride crystals, through the X-ray diffraction (XRD) results show that the product obtained indeed YF3 crystal. By scanning electron microscopy (SEM) and transmission electron microscopy (TEM) characterization of the morphology of the product, that product is nanowire KEYWORDS： Nanowires ，hydrothermal Synthesis，YF3 TOC \o 1-3 \u 目 录 摘 要 PAGEREF _Toc263101329 \h I ABSTRACT PAGEREF _Toc263101330 \h II 第一部分绪论 PAGEREF _Toc263101331 \h 1 1引言 PAGEREF _Toc263101332 \h 1 1.1纳米材料的定义 PAGEREF _Toc263101333 \h 1 1.2 纳米材料的分类 PAGEREF _Toc263101334 \h 1 1.3纳米材料的发展现状 PAGEREF _Toc263101335 \h 2 1.4 纳米产业发展趋势 PAGEREF _Toc263101336 \h 6 1.5纳米技术对传统产业改造 PAGEREF _Toc263101337 \h 8 1.6纳米材料的特殊性质 PAGEREF _Toc263101339 \h 9 2本论文的主要内容和基本理论 PAGEREF _Toc263101341 \h 10 2.1纳米线的相关知识 PAGEREF _Toc263101342 \h 10 2.2 氟化钇的性质、用途、研究现状 PAGEREF _Toc263101343 \h 12 2.3纳米线的制备技术简介 PAGEREF _Toc263101344 \h 13 3.水热技术概述 PAGEREF _Toc263101345 \h 13 3.1水热法的定义及发展 PAGEREF _Toc263101346 \h 13 3.2水热反应中的晶粒结晶机制 PAGEREF _Toc263101347 \h 14 3.3水热法的特点 PAGEREF _Toc263101348 \h 14 第二部分实验部分 PAGEREF _Toc263101349 \h 15 1.本实验制取YF3简介 PAGEREF _Toc263101350 \h 15 2.影响晶粒度的因素 PAGEREF _Toc263101352 \h 15 3.YF3水热合成实验表征方法 PAGEREF _Toc263101353 \h 16 3.1 X射线衍射分析（XRD） PAGEREF _Toc263101354 \h 16 3.2 扫描电子显微镜（SEM) PAGEREF _Toc263101356 \h 16 3.3透射电子显微镜（TEM) PAGEREF _Toc263101359 \h 16 4.