双辊薄带铸轧中心线偏析机理与试验研究-OpenRepositoryof.PDF

25 10 2015 10 Volume 25 Number 10 The Chinese Journal of Nonferrous Metals October 2015 1004-0609(2015)10-2738-07 ( 066004) FeMn 001 Kiss Fe Kiss Kiss TG111.4 A Mechanism and experimental research on centerline segregation of twin-roll strip casting DU Feng-shan, LÜ Zheng, HUANG Hua-gui, XU Zhi-qiang, AN Zhong-jian (National Engineering Research Center for Equipment and Technology of Cold Strip Rolling, Yanshan University, Qinhuangdao 066004, China) Abstract: The problem of casting Al-alloy strip was studied, the mechanism of as-cast strip centerline segregation was analyzed from the perspective of macro and micro, and a mathematical method was developed which completely couples solute field, flow field and temperature distribution. The distributions of Fe and Mn in the Al alloy molten pool were figured out by the mathematical method. The results show that the theoretical calculation agrees well with the experimental results. The solidification structure grows along 001 direction rapidly by the form of columnar crystal. Meanwhile, the solute elements are focused gradually in the kern zone, and the maximum value is gotten at the Kiss point zone. In particular, Fe content of the Kiss point zone is much higher than the average value, and centerline segregation appears after solidification. The centerline segregation tends to increase with the increase of casting speed and roll gap. Key words: twin-roll strip casting; solute field; flow field; centerline segregation; Kiss point 21 [2] [3]