嵌段共聚物长程有序纳米结构的调控.pdf

嵌段共聚物长程有序纳米结构的调控 丛志楠，张良顺 (华东理工大学材料科学与工程学院，上海 200237) Abstract： In order to study the formation mechanism of long-range ordered nanostructures of block copolymers during the process of zone annealing, a new local annealing theoretical model was developed based on dynamic self-consistent field theory to study the self-assembly behaviors of block copolymers in presence of zone annealing. The effects of shifting velocity of propagation fronts and block copolymers composition on the ordering degree of microphase-separated nanostructures were investigated. The results demonstrated that lowing the shifting velocity helps the block copolymers to self-assemble into the long-range ordered nanostructures due to the suppression of thermal fluctuations of phase separation. The surface enrichment near the walls induces the orientation modulation of defect-free nanostructures through tuning the composition of block copolymers. 摘要： 为了研究局域退火过程中嵌段共聚物有序纳米结构的形成机理，基于动态自洽场理论， 发展一种新的局域退火模型，并应用于共聚物引导自组装行为的研究。讨论退火移动速 率和 共聚物组成等因素对纳米结构有序程度和取向调节的影响规律。计算结果表明： 减缓移动速 率有助于有效地压制相分离过程中热涨落，从而获得长程有序纳米图案。 共聚物组成的非对 称性诱导富集层的形成，从而调节无缺陷纳米结构的取向。 嵌段共聚物自组装形成特征尺寸在 30 nm 以下的周期性纳米结构，这种结构在量子点、 磁存储介质的制备和下一代光刻技术的集成上存在潜在应用。由于很难获得长程有序的 纳米结构，目前共聚物的商业应用受到限制。为了实现纳米结构的长程有序，研究者设 计 了多种方案来构筑无缺陷纳米图案，包括固定外场 (如化学和几何模板) 和动态外场 (如剪 切流、电场和热梯度场) 。 在上述方法中，依赖于时间和空间的热梯度法也称为 局域退火法，具有简单，可规模化 连续生产的潜在优势。此方法由于可以快速地制备 共聚物长程有序纳米结构而受到工业界的 重视。局域退火法起源于冶金学，Hashimoto 等[8]将其推广到嵌段共聚物体系。不同于通常 的退火过程，局域退火法是通过限制相 分离畴在狭窄局域生长，从而提高共聚物图案的有序 程度。Berry 等进一步证明了局域 退火法显著地加速纳米结构的有序过程。虽然上述研究 证实了局域退火法可有效地制 备大尺度有序纳米图案，但是并没有阐明有序结构的微观细 节。尤其是局域退火过程 中有序结构的形成机理有待进一步探索。 目前有机白光材料通常是将多种发光材料简 1-3 单共混 ,然后通过每个发光体产生光的混合来实现白光。 该类材料在器件运行过程中 容易在光、热和电等因素作用下产生相分离而产生诸如器件光谱稳定性不高、驱动电压 增大乃至寿命降低等方面的问题 ,这将使材料彻底丧失发光功能。 一方面 ,对有机电致 白光二极管而言 ,平板显示和照明应用对器