耐候钢05CuPCrNi冷加工性能研究.pdf

耐候钢 05CuPCrNi 冷加工性能研究 赵德文 董学新 杜林秀 刘相华 王国栋 ( 东北大学) 翁 宇 贾志鑫 (本溪钢铁公司) 摘 要 研究了耐候钢05CuPCrNi冷轧板的硬化曲线,变形抗力模型,退火后力学性能并给出了理论再结晶温 度初步测试结果.结果表明1.6 与2.0 mm厚冷轧板在600℃退火半小时后其力学性能满足该钢种的技术标准要 求，1.6mm厚冷轧板理论再结晶开始温度为510～520℃, 2.0mm厚冷轧板为520～530℃. 关键词： 耐候钢，硬化曲线，变形抗力模型,再结晶 RESEARCH ON COLD WORKING PERFORMANCE OF WEATHER RESISTANT STEEL 05CuPCrNi PLATE ZHAO Dewen DONG Xuexin DU Linxiu LIU Xianghua WANG Guodong (Northeastern University) WENG Yu JIA Zhixin (Benxi Iron and Steel (Group)Corp.) ABSTRACT The work-hardening curve, deformation resistance model and mechanical properties of annealed weather resisting steel plate were studied, and some preliminary measured results of theoretical re-crystallization temperature were obtained. It has been shown by the results that the mechanical properties of 1.6 and 2.0 mm thickness cold rolled plates satisfy the requirements of the technical standard of the steel when annealed at 600 ℃ for half hour, and the theoretical re-crystallization starting temperature is from 510 to 520℃ for 1.6mm thickness plate and from 520 to 530℃ for 2.0mm thickness plate. KEY WORDS weather resisting steel, work-hardening curve, deformation resistance model, re-crystallization 试验用料.机油冷却润滑条件下冷轧到 2.0mm 与 1 引 言 1.6mm 成品板材.总变形程度大于 30%后加工较困 由于火车、汽车车箱面对介质腐