纳米石墨薄片的制备表征与应用.pdf

纳米石墨薄片的制备、表征与应用 黄摇 琨摇 摇 衣志勇摇 摇 郭摇 静摇 摇 黄渝鸿摇 摇 范敬辉 (中国工程物理研究院总体工程研究所,绵阳摇 621900) 文摇 摘摇 为了获得适宜于同聚合物进行纳米复合的纳米石墨薄片(NGS),采用微波膨化制备膨胀石墨 (EG),利用超声剥离与表面修饰获得NGS,并借助SEM、XRD、FTIR等分析其微观结构。 结果表明:EG 由许多 厚100-300 nm 的石墨薄片连接而成并形成网络结构,孔隙尺寸约几十纳米到几十微米;通过对EG 的超声剥 离可破坏其原有网络结构并将石墨晶片进一步剥离为大量30-60 nm厚的石墨薄片;石墨微波膨化与超声剥 离过程中微观形貌的变化及其表面活性基团的引入,有利于进一步借助插层法实现聚合物与石墨的纳米复合。 关键词摇 膨胀石墨,超声剥离,纳米石墨薄片 Preparation and Characterization of Nanographite Sheets Huang Kun摇 摇 Yi Zhiyong摇 摇 Guo Jing摇 摇 Huang Yuhong摇 摇 Fan Jinghui (Institute of Systematic Engineering,CAEP P.O.Box919-412,Mianyang摇 621900 ) Abstract摇 The expanded graphite was prepared through microwave expanding method and the nanographite sheetswerepreparedthrough ultrasonictreatment and decorationtechnology. The microstructure of expanded graphite and nanographite sheets were characterized by means of SEM, XRD and FTIR. Meanwhile, the application of nanographite sheets in EPDM/ Graphite nanocompositeswere introduced. The results showed that EG aremadefrom a lot of graphite sheetswith 100 to300 nm thickness and formed a kind of net structure. By means of ultrasonic treat鄄 ment,graphite isexfoliatedandbecamemany nanographite sheetswith30 to60 nmthickness,meanwhile,theactive groupsareledintothesurfaceofnanographitesheets. TheapplicationeffectofnanographitesheetsinEPDM/ Graphite nanocomposites are good. Key words摇 Expanded graphite,Ultrasonic delamination,Nanographite sheets 0摇 引言 散形态、提高分散性且并未破坏石墨固有的层状结构 膨胀石墨(EG)由天然鳞片石墨经插层及高温膨 单元,因此,可望实现聚合物与石墨的纳米复合并获 化而成,具有柔软、轻质、多孔、吸附性好、耐高低温、 得更为理想的使用性能。 耐腐蚀、耐辐射、耐氧化、自润滑、抗渗透、高回弹、各 在纳米石墨薄片(NGS)的诸多制备方法中,球磨 向异性等优异特性。 近年来聚合物/ 石墨纳米复合材 法产物纯度不高且生产效率较低,爆炸法工艺复杂且 料已逐步成为聚合物/ 层状无机物纳米复合材料领域 操作条件苛刻,电化学法速度慢且产量较低,激光脉 [1-4] 的一个重要分支并引起学术界广泛关