共固化复合材料铝蜂窝夹层结构性能.PDFVIP

共固化复合材料/ 铝蜂窝夹层结构性能 潘玲英　 　 孙宏杰　 　 尹　 亮　 　 林　 娜　 　 杨智勇 (航天材料及工艺研究所,北京　 100076) 文　 摘　 采用共固化工艺制备了碳纤维增强复合材料面板/ 铝蜂窝夹层结构。 通过考察固化压力对复合 材料面板性能的影响确定了共固化的成型压力,对比分析了不同规格铝蜂窝及其夹层结构的力学性能。 结果 × 表明,对于薄面板,成型压力对面板力学性能的影响较小,规格为0.04 mm 4 mm 的铝蜂窝制备的夹层结构具 有更高的比强度和比刚度,且成型工艺性好。 关键词　 共固化,复合材料,铝蜂窝,夹层结构,性能 Properties of Co-Curing Composite Panel/ Aluminium Honeycomb Sandwich Structure Pan Lingying　 　 Sun Hongjie　 　 Yin Liang　 　 Lin Na　 　 Yang Zhiyong (Aerospace Research Institute of Materials Processing Technology,Beijing　 100076) Abstract　 Composite panel/ aluminiumsandwich structurewasfabricatedbytheco-curingprocess. Theeffectof processing pressure on the properties of composite panel was investigated to determine the co-curing pressure. The properties of aluminium honeycomb with different dimension parameter and their sandwich structures were also tested and analyzed. Theresultsshow that theprocessingpressurehaslittle effect onthepropertiesof thin compositepanel. × The sandwich structure fabricated by the aluminium honeycomb of 0.04 mm 4 mm has high specific strength and modulus,and is easier to fabricate. Therefore,it has more widely potential applications. Key words　 Co-curing,Composite,Aluminium honeycomb,Sandwich structure,Property 0　 引言 影响确定了共固化的成型压力,并对不同规格铝蜂窝 蜂窝夹层结构具有质量轻、比强度和比刚度高、 芯材及其夹层结构性能进行了对比分析,优选出工艺 抗疲劳等优点,因此广泛应用于航空航天领域,如运 性及综合性能最优的夹层结构。 载火箭有效载荷整流罩、卫星太阳能阵列基板、航天 1　 实验 - 飞机的舱盖、飞机的机翼等[1 4 ]。 其中碳/ 环氧复合 1.1　 原材料 材料面板与铝蜂窝组成的夹层结构更为受人关 MT300/ 603预浸料,自制;铝蜂窝芯材,规格(铝 [4 ] × × 注 。