煉鋁爐渣高鋁耐火磚熱特性之研究 T he rma l Pro pe rt ies of Hig h A lumina Ref ractory De rived f rom Aluminum Dross and Ash 1 1 S.F. Yang, T.M. Wang B oth alum inum dr o ss an d a sh h av e b een recycled to manufacture high alumina refractory, aluminum hydroxide and aluminum oxide. Although the development of commercial size of alumina ( ) refractory (230 114 65 mm) is completed and (230 114 the capacity of commercial manufacturing process 65 mm) for producing alumina refractory is higher than 1,000 1000 pieces/batch, the extensive thermal properties of the alumina refractory need to be determined. In this work, we developed test methods to measure the thermal properties such as reheat shrinkage, r e fr a ct or in e s s an d so ft en in g t emp er at u r e o f refractoriness under load. The fire resistant, suitable op erating temp erature and application category of alumina refractory can be clearly def ined by ( ) measured thermal properties. We also assessed the environmental benef it including greenhou se gas emission. 關鍵字： Key words: Aluminum dross, Aluminum ash, High Aluminnum refractory, Refractoriness, Environmental benefit 一、前　　言