Mechanical properties of the hypo-(hyper-)eutectic steel 亚（过）共析钢的珠光体力学性能 2)Granular Pearlite 球状珠光体 Performance depends on: (1) F grain size (substrate) (2) Fe3C size, quantity, distribution. Fe3C small, uniform distribution, the strength, hardness, toughness is also ↗. ????? Compared with the same component flake P: the hardness is slightly lower, higher toughness 性能取决于： （1）F晶粒大小（基体） （2）Fe3C大小、数量，分布。 Fe3C 细小，分布均匀， 则强度、硬度较高，韧性也↗。 与同成分片状P相比：强度硬度稍低，塑韧性较高 Nucleation + Growth Because it is a two-phase mixture, so there is a problem about leading phase. 因为是两相混合物，因此有一个领先相的问题。 1) leading phase ?????? Related to chemical composition ?????? Hypoeutectoid steel: F ?????? Hypereutectoid steel: Fe3C ?????? Eutectic steel: both can be, is generally considered to be Fe3C In the presence of insoluble cementite in austenite, the transition of P is promoted. 2.Pearlite transformation (1)lamellar pearlite 2) Formation mechanism 形成机理（以共析钢为例） A → F + Fe3C 0.77% 0.0218% 6.69% fcc bcc 复杂正交 形核： 在A晶界和缺陷密集区，形成薄片状Fe3C晶核。 长大：扩散进行 长大方式：纵向长大，沿着珠光体片长轴方向长大； 横向长大，沿着珠光体片垂直方向长大 依靠C的扩散 界面过程， 依靠Fe的自扩散 Carbon diffusion mechanism of the slice pearlite growth 片状珠光体长大碳的扩散机制 CA/F：A/F界面上A一侧的碳浓度 CA/ Fe3c ：A/Fe3C界面上A一侧的碳浓度 CA：原A中的碳浓度 CF/A： F/A界面上F一侧的碳浓度 CF/ Fe3c ：F/Fe3C界面上F一侧的碳浓度 C Fe3c ：Fe3C的碳浓度为6.69% CA/F Fe3C F A1 CA CA/ F T C Fe3c F △T A CA/Fe3c CF/A CF /Fe3c A CA/ Fe3C 2.Pearlite transformation (1)lamellar pearlite 2.Pearlite transformation (1)lamellar pearlite Due to the difference between the concentration of each phase, resulting in the following diffusion: 由于各相间的浓度差，造成了如下扩散： （a）interface diffusion界面扩散 在t1温度时，奥氏体中CA/FCA/Fe3C，造成碳从A/F界面扩散到A/Fe3C界面，这便破坏了界面平衡，使CA/F↘,CA/Fe3C↗，进而导致F长大(使CA/F ↗)，Fe3C长大(使CA/Fe3C ↘)。 （b）Away from the P zone 由远离P区扩散 因为CA/FCACA/Fe3C，F前沿的碳将向远处扩散，而远处的碳(浓度为CA)将扩散至Fe3C前，使F、Fe3C长大。 （c）Diffusion of C in ferri