TOFD超声波射时差法.ppt

* For the parallel scan, which is across the weld section, the path to the defect tip varies with the probe position because of the changing of the path lengths. This variation generates an inverted parabola curve which is typical for TOFD parallel scans. The path to the defect reduces to a minimum when the probes are positioned symmetrically over the defect. This allows for an accurate measure of the defect’s depth as discussed earlier. The parallel scan allows also to determine the lateral position of the defect. The minimum wave path indicates the place were both probes are symmetrical positioned over the defect. At this location the defect lies thus straight in the middle of both probes. For this purpose the software enables the drawing of locus curves that will be shown during the demo. * * * * * TOFD的优点 对于焊缝中部缺陷检出率很高 容易检出方向性不好的缺陷 可以识别向表面延伸的缺陷 通过时间检测缺陷的信号 和脉冲反射法相结合时效果更好 中国工业检验检测网 TOFD 的局限性 在外表面附近有约3mm的盲区 内表面附近也可能存在盲区 对“噪声”敏感 夸大了一些良性的缺陷, 如气孔, 未熔合。 中国工业检验检测网 应用 TOFD 技术检测到的缺陷信号 中国工业检验检测网 近表面裂纹 裂纹上尖端信号将直通波信号打断 2 1 X形坡口中部未焊透 上下尖端都有明显的信号 1 2 3 4 中国工业检验检测网 根部未焊透 直通波的相位与缺陷相位相同 1 2 3 中国工业检验检测网 侧壁未熔合 能够清晰的看到上下尖端信号 1 2 3 4 中国工业检验检测网 气孔 气孔信号或单个出现，或成串的出现 1 2 中国工业检验检测网 横向裂纹 能够看到裂纹的宽波束信号 1 2 3 4 1 2 3 中国工业检验检测网 根部内凹 内壁反射信号发生扭曲 1 2 3 中国工业检验检测网 层间未熔合 中国工业检验检测网 二、TOFD在压力容器制造过程中现场应用 3、现场缺陷数据分析 裂纹1 （08R018 TK101A F6 7.14m） TOFD数据分析结果：H=28.1mm ⊿H=9.8mm 位置= 174.1mm L = 323.2mm（焊缝位置偏心） 中国工业检验检测网 二、TOFD在压力容器制造过程中现场应用 3、现场缺陷数据分析 裂纹2（08R063 R713 A10 0.3 H=29 L=40 III级 UT H=28 L=35 SL+13dB III级 中国工业检验检测网 二、TOFD在压力容器制造过程中现场应用 3、现场缺陷数据分析 裂纹2（08R063 R713 A10 0.3 H=29 L=40 III级 UT H=28 L=35 SL+13dB III级 中国工业检验检测网 、TOFD在压力容器制造过程中现场应用 3、现场缺陷数据分析 裂纹3（08R018 D203 F2 11.350 中国工业检验检测网 * * Since TOFD is based upon diffraction it is useful to first explain what is meant