聚醋酸乙烯酯团块共聚物之制震材料与黏弹特性-eTop-工程科技推展.PDF

行 料 精 類 行 年年 行 理 利 年 年 含聚丙烯酸丁酯-聚醋酸乙烯酯團塊共聚物之制震材料與黏彈特性 Damping and viscoelastic properties of materials containing poly(butyl acrylate)-b-poly(vinyl acetate) 計劃編號： NSC 97-2221-E-035-042 執行期間：97 年 08月 01日至 98 年 7月 31日 計劃主持人：朱侯憲 逢甲大學化工系 計畫參與人員：徐子越 逢甲大學化工系 Abstract Living free radical polymerization initiated by n‐Dodecyl mercaptan and  ε‐Caprolactam was performed to prepare the diblock copolymer of PBA‐PVAc.   In preparing the PBA macro initiator, the reaction can only reach 60% conversion  in 6 hours and levels‐off then. To prepare the PBA‐PVAc diblock copolymer, it requires  a reaction temperature of 75℃.  To improve the polymerization rate, the addition of monomer was divided into  two stages, so as to increase the collision probability of initiator to monomer at the  initial stage to ensure high reaction probability. We tried to raise the temperature to  140℃ at the first hour to speed the process of the reaction, but it reduced the  proportion of the living polymerization, and the reaction became dead‐end in later  period. It is suggested to run the polymerization at 75℃ to increase the proportion  of living polymerization.      The PBA‐PVAc diblock copolymer has two Tg’s , as confirmed by DSC analysis.   Since the PBA block is considerably larger than the PVAc block we can’t observe the  higher Tg’s in RDA test, where the higher temperature tanδ peak is covered by the  lar