物性表_赛拉尼斯 Celanese PA66 CELSTRAN® PA66-GF50-20 AD3007 PA66 Glass Reinforced.pdfVIP

CELSTRAN® PA66-GF50-20 AD3007 | PA66 | Glass Reinforced Description Material code according to ISO 1043-1: PA66 Heat stabilized Nylon 66 reinforced by 50 weight percent long glass fibers. The pellets are cylindrical and normally as well as the embedded fibers 11 mm long. Parts molded of CELSTRAN have outstanding mechanical properties such as high strength and stiffness combined with high heat deflection. The notched impact strength is increased at elevated and low temperatures due to the fiber skeleton built in the parts. The long fiber reinforcement reduces creep significantly. The very isotropic shrinkage in the molded parts minimizes the warpage. Complex parts can be manufactured with high reproducibility by injection molding. Can be used for substituting die cast metal with the advantage of Weight reduction, no corrosion problems, no post treatment. Physical properties Value Unit Test Standard Density 1570 kg/m³ ISO 1183 Mechanical properties Value Unit Test Standard Tensile modulus (1mm/min) 16500 MPa ISO 527-2/1A Tensile modulus (80°C) 10000 MPa ISO 527-2/1A Tensile strength (80°C) 165 MPa ISO 527-2/1A Tensile stress at break (5mm/min) 250 MPa ISO 527-2/1A Tensile strain at break (5mm/min) 2 % ISO 527-2/1A Elongation at break (80°C) 2.7 % ISO 527-2