交流阻抗法可以测定腐蚀速度,并可以研究金属腐蚀状态,表面氧化膜或腐蚀产物膜的形成与破坏,缓蚀剂的吸附行为及作用机理等。 钼钢阳极行为分析试验： 从稳定电位随电位提高，EIS从规整半圆向半圆变小、低频出现第2个半圆、出现直线段等发展。 问题： 1)如何求腐蚀速度？ 2)EIS变化说明什么？ 3)电位再提高EIS会怎样？为什么？如何证明？ 钼钢在碱性溶液中的阳极极化曲线及不同电位下的交流阻抗谱 Surface micrographs of different electrolysis time for the DSA anode prepared at 400℃. (b) non-electrolysis, (c) after degradation (900h). 交流阻抗法研究DSA电极表面特性及其阳极失效过程 Variations of potential with operation time during the accelerated electrolysis test of DSA anode in 0.5M H2SO4 solution. Tafel slopes of DSA as function of electrolysis time for OER. Electrolyte: 0.5M H2SO4 Experimental EIS patterns for DSA electrodes with various electrolysis time in 0.5M H2SO4 solution at 1.35V (SCE): (a) Nyquist diagrams; and (b) Bode plots. 等效电路: Rs(RfQf)(RctQdl) EIS (a) The Rf and Qf values in 0.5M H2SO4 solution as a function of electrolysis time in DSA electrodes prepared at 400℃. (b) The Rct and Qdl values in 0.5M H2SO4 solution as a function of electrolysis time in DSA electrodes prepared at 400℃. (a) (b) 刊印在《 Electrochimica Acta 》上的1篇文章 (IF:2.955). 刊印在《Solid State Sciences 》的1篇文章(IF:1.752) 刊印在《Journal of Electroanalytical Chemistry》的1篇文章(IF:2.5) 思考题 1.如何设计可突出研究电极进行交流阻抗测量？测量溶液电导、电极/溶液界面电容有何要求？ 2.如何用交流阻抗法测定交换电流或金属腐蚀速度？说明原理及方法。 3.说明纯电阻、电容、电感的阻抗谱特征。 4.法拉第阻抗Rp、双电层电容Cd（或电感L）及溶液电阻Rl的串并联电路有怎样的阻抗谱？从谱图如何求得电极体系的Rl、Rp、Cd ？ 5.描述弥散效应一般用常相位角元件（CPE）, 何谓CPE？ 第7章完 第7章 交流阻抗测试方法 孟惠民 电化学研究方法及实验课程 §7.1 交流阻抗法概述 §7.2 电化学极化下的交流阻抗 §7.3 浓差极化下的交流阻抗 §7.4 复杂体系的交流阻抗 §7.1 交流阻抗法概述 交流阻抗法(EIS) 交流阻抗法是指小幅度对称正弦波交流阻抗法。就是控制电极交流电位（或控制电极的交流电流）按小幅度（一般小于10毫伏）正弦波规律变化，然后测量电极的交流阻抗，进而计算电极的电化学参数。 由于使用小幅度对称交流电对电极极化，当频率足够高时，以致每半周期所持续的时间很短，不致引起严重的浓差极化及表面状态变化。而且在电极上交替地出现阳极过程的阴极过程，即使测量讯号长时间作用于电解池，也不会导致极化现阶段象的积累性发展。因此这种方法具有暂态法的某些特点，常称为“暂稳态法”。“暂态”是指每半周期内有暂态过程的特点，“稳态”是指电极过程老是进行稳定的周期性的变化。 交流阻抗法适于研究快速电极过程，双电层结构及吸附等，在金属腐蚀和电结晶等电化学研究中也得到广泛应用。 电解池的等效电路 当用正弦交流电通过电解池进行测量时，往往可以根据测量体系的不同把电解池简化为不同的等效电路 所谓等效电路就是由电阻R和电容C所组成的这样的电路：当加上相同的交流电压讯号时，通过此等效电路中的交流电流与通过电解池的交流电流具有完全相同的振幅和相位角。 交流电通过电解池时，将双电层等效地看作类似电容器的容抗，电极本身、溶液及电极反应所引起阻力看成阻抗，