木材化学镀镍老化镀液的再生与回用-电镀.pdf

木材化学镀镍老化镀液的再生与回用 王立娟 李坚 连爱珍 (东北林业大学材料科学与工程学院，哈尔滨 150040) 摘要：本文采用可溶性钙盐沉淀去除施镀木材的化学镀镍废液中的亚磷酸根离子，再用氟化物去除 残余的钙离子。主要研究了 pH 值、钙离子与亚磷酸根的浓度比、处理温度和时间对亚磷酸根去除 率的影响。采用再生处理后的镀液施镀木材，可以得到具有良好导电性和电磁屏蔽性能的镀层。 关键词：化学镀镍，木材，废液再生，导电性，电磁屏蔽 Regeneration and Reuse of Exhausted Solution of Electroless Nickel Plating Wood Veneer/ Wang Lijuan, Li Jian, Lian Aizhen(Northeast forestry university, Harbin 150040, P. R. China)//Journal of Northeast Forestry University.-2005,33(3).- The regeneration of exhausted solution of electroless nickel plating wood veneer was realized by using soluble calcium salt to precipitate and remove phosphite and then using fluoride to remove residual calcium ions in the solution. The effects of pH value of solution, treatment temperature and concentration ratio of calcium ion to phosphite ion on the removal efficiency of phosphite were investigated. Wood veneer was electroless plated by using regenerated solution and the coating with better electric conduction and electromagnetic shielding properties was obtained. Key words Electroless nickel plating; Wood; Regeneration of exhausted solution; Electric conduction; Electromagnetic shielding 以次亚磷酸钠为还原剂的化学镀镍技术已有50 多年的历史。化学镀法也是非金属金属化的主要 途径之一，在许多领域广泛应用。不过，化学镀木材的研究在国内少见。无论在哪种基材上进行化 学镀，由于施镀过程中镍离子被还原的同时，次亚磷酸盐被氧化成亚磷酸盐，经过不断的累积，将 造成镀液中的镍离子与亚磷酸根生成亚磷酸镍沉淀，易导致镀液的分解。 在化学镀镍的废液中，除了含有较高浓度的镍离子、亚磷酸根离子和次亚磷酸根离子外，还含 有一定量的络合剂、缓冲剂和稳定剂等成分。这些都是国家监控的污染物，另外镍又是一种紧缺资 源。因此，无论是从节约资源，还是从环保、降低化学镀镍的成本角度出发，化学镀镍废液的净化、 再生并重新利用都是非常有意义的[1] 。 本研究是利用氯化钙沉淀法对施镀落叶松单板的化学镀镍废液进行净化、再生，并以再生后的 废液施镀落叶松单板，研究镀后落叶松单板的导电性和电磁屏蔽性能。 1.原理 化学镀镍液长时间施镀后，其中的亚磷酸根离子、钠离子、硫酸根离子及其他副产物逐渐积累， 当达到一定浓度时，便影响镍、磷沉积。 2+ - - + Ni + H PO + H O → Ni + H PO + 2H 2 2 2 2 3 用氯