硫酸脲氨化法生产尿基复合肥工艺技术及应用.docVIP

( 中国 － 阿拉伯化肥有限公司 秦皇岛066003)摘 ( 中国 － 阿拉伯化肥有限公司 秦皇岛 066003) 摘要 对硫酸脲氨化法生产尿基复合肥工艺的原理和影响造粒的主要因素进行了分析。总结了生产过程 中出现的主要问题，并提出解决办法和应对措施，这为蒸汽团粒法、尿液喷浆法、氨酸法造粒装置技术升级和改 造提供了可借鉴的思路。 关键词 硫酸脲 氨化造粒 尿基复合肥 技术改造 Application of Technology for Production of Urea-Based Compound Fertilizers by Ammoniation of Urea Sulfate Shi Xueyong，Zhang Yanxu ( Sino-Arab Chemical Fertilizer Co．，Ltd． Qinhuangdao 066003) Abstract An analysis is made of the principle and main factors affecting granulation in the production of urea-based compound fertilizers by ammoniation of urea sulfate． The main problems in production are summed up， and ways of settlement and countermeasures are proposed， thereby providing thoughts for reference in the technological upgrading and renovation of the granulation unit based on steam agglomeration，urea solution spheroidizing and ammonia-acid method． Keywords urea sulfate ammoniation granulation urea-based compound fertilizers technology renovation 随着我国复合肥和复混肥标准的分别制订和 实施，我国蒸汽团粒法和尿液喷浆法复混肥生产 工艺急需改造，升级为有化学反应的复合肥生产 工艺，目前一般采用最简单的氨酸法。但是氨酸 法主要适用于高浓度磷肥和平衡型肥料的生产， 工艺适应性不强。随着对硫酸脲氨化法生产复合 肥工艺技术研究的不断深入，已有多家生产企业 采用硫酸脲氨化工艺进行了工业化的生产并取得 了成功，同时在生产中也暴露出一些问题。笔者 经深入分析研究，提出了解决办法和改进措施，并 取得了满意的效果。 H2 SO4 -H2 O 三元系统相图，并提出尿素与硫酸反 应可以形成不同的加合物和低温共熔物，最低共 熔点为 10 ℃ 。 尿素与硫酸的加合反应过程属于放 热 反 应， 且第 1 个摩尔尿素与硫酸结合时放出大量热量， 导致温度剧升，而第 2 个摩尔的尿素溶解时放热 较少。另外，由于尿素与硫酸加合过程的放热，酸 解液配制时所产生的热量可能使系统过热而发生 缩合等副反应，甚至引起爆炸，因而要求酸解液配 制温度不得超过 130 ℃ ，一般控制在 110 ℃ 以下， 并在配制过程中控制合适的尿素与硫酸的摩尔比 例，同时加入适量的水以降低硫酸脲的黏度和保 持硫酸脲的稳定。 1 硫酸脲氨化法生产尿基复合肥工艺原理 1． 1 硫酸脲的基本性质 1934 年，Dalman． L 等 研 究 了 CO ( NH 1． 2 硫酸脲溶液的配制 固体尿素由破碎机破碎大块后经斗提机进入 ) - 硫酸脲溶液，然后将其用泵送至造粒系统。在配增多。不同的物料体系成粒性与液相量密切 硫酸脲溶液，然后将其用泵送至造粒系统。在配 增多。不同的物料体系成粒性与液相量密切相 制过程中，通过外置换热器用冷却水降温，以使硫 酸脲溶液温度保持在正常操作范围内。 关，在相同的生产条件下，尿素 － 磷酸铵系物料较 其它物料体系的含水量要求更低，最佳的含水质 量分数在 3% 左右。 ( 2) 温度的影响 造粒温度提高，盐分之间的化学反应 变 得 活 跃，物料间化学键结合的机会增加。而且无机盐 的溶解度一般随温度的升高而增大，所以造粒温 度高时，体系的液相量随之增多，相互的溶解和反 应生成复盐量增加、均匀程度提高，此时外加液相 量应适当减少，造粒湿含量( 水分) 应随温度和原 料的溶 解度变化而调整。如尿磷铵造粒温度由 60 ℃ 调整为 90 ℃ 时，其物料含水质量分数应从 3． 2%