《刚玉Cr18-Ni8钢钎焊界面组织研究》-毕业论文（设计）.docVIP

PAGE 刚玉/Cr18-Ni8钢钎焊界面组织研究 （陕西理工学院 材料科学与工程学院材料成型及控制工程专业084班；陕西.汉中723003） 指导老师： [摘要] ：先进结构陶瓷（刚玉）具有优异的高温力学性能，而金属材料具有良好的塑性及其可加工等性能，将两种材料连接起来可用于有特殊要求的场合，对先进结构陶瓷（刚玉﹑SiC等）与金属材料（Cr18-Ni8钢）的钎焊连接工艺﹑钎料接头性能等方面的研究进行了综述，并对陶瓷与金属钎焊链接技术的发展方向进行了展望。 [关键字] ：刚玉；Cr18-Ni8钢；钎焊；界面组织研究 Interfacial microstructure of corundum / Cr18-Ni8 steel brazing （Grade08,Class04,Major material forming and control engineering，School of Materials Science and Engineering Dept.，Shaanxi University of Technology，Hanzhong 723003，Shaanxi) Tutor: Abstract：Advanced structural ceramics possess good high-temperature mechanical properties, and metal materials own good ductility and processability, etc. To weld the two materials could meet special needs, the recent development of the brazing joining technology of some typical advanced structural ceramics inclucting corundum, SiC,etc. and metal materials incluting Cr18-Ni8 alloy and the joint properties are reviewed. Their development is viewed. Key words：Corundum; Cr18-Ni8 steel; Brazing; Interfacial microstructure 第 PAGE 20 页 共20页 目录 中文摘要 Abstract TOC \o 1-3 \h \z \u 1引言 1 1.1研究目的及意义 1 1.1.1研究目的： 1 1.1.2研究意义： 2 1.2相关领域研究现状、发展趋势及应用领域 2 1.2.1研究现状 2 1.2.2发展趋势 3 1.2.3应用领域 4 2试验方法及设备 4 2.1实验选用材料 4 2.2实验方案 4 2.3实验设备 5 2.4实验材料 5 3刚玉/Cr18-Ni8钢钎焊试样的制备 5 3.1焊接工艺设计 5 3.1.1钎焊接头的设计 5 3.2焊前的准备工作 6 3.2.1工件表面处理 6 3.2.2陶瓷表面金属化 6 3.2.3 Cr18-Ni8钢表面处理 10 3.2.4钎料的选择 11 3.3钎剂的选择 12 3.3.1钎剂 12 3.3.2钎剂的作用 13 3.3.3钎剂的选择结果 13 4实验过程 13 4.1钎焊试样制备的具体过程 13 4.2金相试样制备 14 5实验结果与分析及其改进措施 14 5.1实验结果 14 5.2结果分析 15 5.3改进措施 15 5.3.1焊接方法的改进 15 5.3.2钎料的改进 16 6结论 16 参考文献 18 致谢 20 1引言 随着现代科技的迅猛发展，机械设备零件对所用材料性能的要求越来越高，要求材料具有更高的耐磨性、抗蚀性和耐高温等性能。磨损和腐蚀成为零件失效、能源损失的重要原因。当今工业社会近三分之一的能源消耗于磨损、腐蚀之中。零部件的破坏往往自表面开始，表面的局部破坏又导致整个零件失效。金属材料表层的物理化学性能对其许多重要性能，如硬度、耐磨性、耐蚀性、耐热性和抗氧化性等都有决定性的作用。金属陶瓷涂层改变金属基体外表面的形貌、结构和化学组成，并赋予基体新的性能。金属与陶瓷材料各有其独特的优异性能和明显的性能弱点，如何把金属与陶瓷材料各自的性能优势结合起来，多年来一直是材料科学与工程界研究的重点方向之一。 刚玉（Al2O3陶瓷）的熔点为 20