混凝土耐久性概述.docVIP

混凝土耐久性概述 摘要：混凝土是全世界应用最广，使用最多的建筑材料,人们对它的研究已经涉及到各个方面。混凝土耐久性是混凝土诸多特性中非常重要的特性之一。影响混凝土耐久性的因素主要有混凝土碳化，钢筋锈蚀，碱-集料反应，混凝土冻融破坏，氯离子对混凝土的侵蚀等。本文简要综述了主要的几个影响因素的破坏原理以及相关知识，并提出了提高混凝土耐久性的方法。本文所涉及的混凝土耐久性的知识仅是混凝土特性的冰山一角，希望对研究混凝土人士有些帮助。 关键字：混凝土耐久性 主要影响因素 破坏原理 混凝土 Abstract: concrete is the building materials which is most widely used and Used largest number in the world, The people researched it at all espects. Durability of concrete is one of very important characters. What affect the durability of concrete including mang factors,the main factors,for example, carbonation of concrete,corrosion of steel bar, alkali-aggregate reaction, Concrete freeze-thaw destruction , Concrete erosion by Chloride ions ,and so on.This article simply Comprehensive description the main factors’ destruction principles and relevant knowledge,and raise a method which can improve the durability of concrete. Of course,the knowledge of the article refer to, about durability of concrete it is a the tip fo the iceberg, the author hope the article is useful to the man who is Specialized researcher . keyword: durability of concrete main factors influencing destruction principle concrete 1.混凝土耐久性的概念和研究混凝土耐久性的意义。 混凝土的耐久性是指混凝土在实际使用条件下抵抗各种破坏因素的作用，长期保持强度和外观完整性的能力。混凝土的耐久性主要包括抗渗、抗冻、抗侵蚀、炭化、碱骨料反应及钢筋锈蚀等。混凝土是当今世界用量最大的建筑材料。我国混凝土使用量居全球之冠，年用量达20亿t，为适应经济快速发展发挥了极其重要的作用。耐久性对工程量浩大的混凝土工程来说意义非常重要，若耐久性不足，将会产生极严重的后果，甚至对未来社会造成极为沉重的负担。如不少工程在使用10～20 年后，有的甚至在使用几年之后即需维修。另外，混凝土工程大多是永久性的，工程量大、耗资多，若耐久性不良将会给国家财政和社会经济的发展带来沉重的包袱。因此，从资金节约、资源的有效利用及环境保护等方面综合考虑，必须深入研究混凝土的耐久性问题。 2.影响混凝土耐久性的因素以及其破坏原理 影响混凝土耐久性的因素很多，从混凝土结构耐久性损伤的机理来看，分为化学作用引起的损伤和物理作用引起的损伤两大类。另外，生物作用对混凝土耐久性也有一定作用。 化学作用包括：混凝土碳化，钢筋锈蚀，碱-集料反应，混凝土腐蚀等。 物理作用包括：混凝土冻融破坏，冲刷磨损等。 2.1 混凝土的碳化 混凝土碳化是混凝土中的碱与环境中的二氧化碳发生反应生成碳酸钙的过程，它 使混凝土的碱性降低，从而失去对钢筋的保护作用，是混凝土在一般大气环境中钢筋锈蚀的前提条件。衡量混凝土碳化的指标为碳化深度。 混凝土的碳化图1 混凝土的碳化图2 混凝土碳化的主要化学反应式如下： CO2+H2OH2CO3 (1-1) Ca(OH)2+H2CO3CaCO3+2H2O (1-2) 2. ①.混凝土本身的密实度：混凝土密实度越大，碳化速度越慢；