c1181-91中文版-耐化学性聚合物机械灰浆压缩蠕变标准试验方法.docVIP

C 1181 PAGE 784 Designation: C 1181-91 (Reapproved 1996)ε1编号：C 1181-91（1996年重新审批）ε1 PAGE 778 Standard Test Methods for Compressive Creep of Chemical-Resistant Polymer Machinery Grouts1耐化学性聚合物机械灰浆压缩蠕变标准试验方法 These test methods are under the jurisdiction of ASTM Committee C-3 on Chemical-Resistant Nonmetallic Materials and are the direct responsibility of Subcommittee C3.01 on Test Methods. 本试验方法由ASTM委员会C-3抗化学腐蚀非金属材料委员会管辖，并由C3.01试验方法分委会直接负责。Current edition approved May 15, 1991. Published July 1991.现行版本于1991年5月15日批准，并于 This standard is issued under the fixed designation C 1181; the number immediately following the designation indicates the year of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A superscript epsilon (ε) indicates an editorial change since the last revision or reapproval.本标准以固定编号C 1181刊发；紧随编号后的数字表示最初采用的年份，或者是修订版的最后修订年份。圆括号中的数字表示最新重新批准的年份。上标(ε)表示自上一修订版或重新批准后的编辑性修改。 ε1 Note—Keywords were added editorially in September 1996.ε1注——于1996年9月编辑添加关键词。 Scope适用范围 1.1 These test methods cover a quantitative, comparative test for compressive creep of chemical-resistant grouting materials under a sustained load at a test temperature. Constant load is maintained using a torqued bolt and spring washers. Measurements are made at laboratory temperature after exposure periods at the selected test temperature.本试验方法包括大量在持续施加负载情况下以及在试验温度中进行的耐化学腐蚀灰浆材料压缩蠕变比较试验。使用扭矩螺栓或弹簧垫圈维持负载不变。在选定的试验温度下进行曝光后在实验室温度中进行的测量。 1.2 Test Method A outlines the molding techniques for an unbonded test specimen. Test Method B covers the molding techniques for a bonded test specimen.试验方法A对非粘试样的成型工艺进行说明，而试验方法B涉及粘试样的成型工艺。 1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.本