焊接材料 DIN 8555 标准.docVIP

Example Fidur 23/250 E 23 UM 250 CKNPTZ 1 2 3 4 5  1 Short symbol for manual arc welding 2 Shortsymbol Alloy group and application 1 Unalloyed up to 0.4% C or low-alloyed up to 0.4% C and up to max. 5 % alloy constituents Cr, Mn, Mo, Ni in total; soft surfacing, e. g. fill-up welding, buffering layers 2 Unalloyed with more than 0.4% C or low-alloyed with more than 0.4%C and up to max. 5% alloy consitutents Cr, Mn, Mo, Ni in total; running wheels 3 Alloyed, with the properties of hot working steel, hot working tools 4 Alloyed, with the properties of high-speed steel, cutting tools, mandrels, shear blades, cutters, drill bits 5 Alloyed with more than 5% Cr and low C-content (up to approx. 0.2%C) for scale-resistant (also against sulphurous gases) and from 12% Cr-content corrosion-resistant surfacings, e. g. valve parts, plungers, furnace parts 6 Alloyed with more than 5% Cr and higher C-content (approx. 0.2 - 2.0% C) cutting tools, shear blades, rollers for cold rolling mills 7 Mn austenite with 11 to 18% Mn and more than 0.5% C and up to 3% Ni surfacings on large surfaces, e. g. wear plates, jaw plates, digging teeth, bolts 8 Cr-Ni-Mn-austenite crusher parts for medium stress, switch tongue, rails, water turbine parts 9 Cr-Ni-steel (corrosion and heat resistant) corrosion and heat resistant surfacings 10 High C-content and high Cr-alloyed with and without additional carbide former, repairs on mining and steel plant equipment, surfacing on machine parts in the construction industry and agriculture, overburden excavators, sinter crushers 2 20 Co-based, Cr-W-alloyed, with or without Ni and Mo fittings of all tpyes, valve seats of exhaust valves in combustion engines, valve seats of steam engines, pump shafts and similar parts which are exposed to heavy corrosion and erosion 21 Carbide-based (sintered, cast or folled) tools and machine parts for working in stony earth, drills and similar tools, press schrews in the ceramic industry 22 Ni-based, Cr-alloyed, Cr-B