mft8非调质钢螺栓的形变强化效应.pdf

冷作硬化非调质钢螺栓的形变强化效应 Deformation Strengthening Effect of Microalloyed Steel for Cold Heading Bolt 蔡 璐，王章忠，赵秀明，贺显聪 （南京工程学院材料工程学院，南京 211167 ） CAI lu,WANG zhang-zhong, ZHAO xiu-ming, HE xian-cong (School of Materials Science and Engineering, Nanjing Institute of Technology, Nanjing 211167, China) 摘要：根据形变强化非调质钢螺栓的制造工序，对 MFT8 非调质钢原材料、冷拔和 时效处理三种状态下的形变强化效应进行了研究，比较了它们的形变硬化指数及力 学性能，研究分析了组织对其性能的影响。实验结果表明：MFT8 非调质钢形变强 化效应明显；时效处理后仍具有良好的形变强化能力，可以确保螺栓在使用时的安 全性；强化后的螺栓各项力学性能指标达到 8.8 级技术要求，研究材料能够取代调 质钢制造高强度螺栓。 关键词：形变强化；非调质钢；螺栓 中图分类号：TG111.7 ,TG142 Abstract ：According to manufactured procedures of the MFT8 bolt for microalloyed steel, deformation strengthening effects for Raw material, cold-drawing and aging treatment have been studied, respectively. strain hardening exponents and mechanical properties are compared, and the effects of material properties on microstructures are analyzed. The results show that deformation strengthening effect of the MFT8 bolt for microalloyed steel is obvious. It still possesses favorable deformation strengthening performance after aging treatment to insure the use safety of bolts. The standard of all kinds of mechanical properties of deformation strengthening bolt has reached 8.8 grade, therefore, the MFT8 for microalloyed steel can substitute quenched and tempered steel for manufacturing high-strengthened bolts. Key words ：Deformation strengthening ；microalloyed steel ；blot 标准件螺栓在工程及机械领域中用量大、范围广，形变强化非调质钢制造 8.8 级高强度螺栓可省去调质处理工艺，减少热处理工序和设备，降低能源消耗，缩短 生产周期，同时避免了在热处理过程中由于变形或淬火裂纹所造成的废品，具有广 阔的应用前景[1-4] 。 通常用形变硬化指数 n 表征材料的形变强化能力，n 值越大，均匀变形量越大， 冷成形性能好，强化效果明显。非调质钢螺栓的主要生产流程为：热轧线材-酸洗- 冷拔-滚丝- 时效，原材料经冷拔后形变强化，其力学性能如何，能否取代调质钢制 造高强度螺栓，时效后的形变强化的余量能否确保螺栓使用的安全，需要进行实验 研究。 1 实验材料和方法 MFT8 钢原材料为φ9mm 的热轧线材，化学成分 ( 质量分数%)为：C0.21 ，Si 0.13 ，Mn1.37 ，P 0.015