铝的阳极氧化和着色--2014.4.21.pdf

铝的阳极氧化和着色 -添加剂甘油对氧化膜性能的影响 摘要 电解质种类、电流密度、通 电时间、温度以及添加剂等因素对氧 化铝多孔膜的形成过程有 著影响。 电解液中加入甘油作为添加剂, 不但可以增加阳极氧化形成的多孔膜的厚度,而且有利于增强氧化膜 的韧性。本文在固定其它因素为文献最优值的情况下，探究甘油用量 对铝的阳极氧化的影响。采用高纯铝作阳极,铅网作为阴极,在硫酸溶 液中进行恒压阳极氧化，以铝片的着色效果、耐腐性、膜厚测定为表 征手段。结果发现, 表明添加一定量的甘油能增强氧化膜的性能，但 添加量多了反而会减低氧化膜性能。对于氧化膜不同的性能方面随甘 油添加剂用量的变化程度有待近一步探究。 关键词 ：氧化铝多孔膜 阳极氧化 有机添加剂 甘油 Abstract The properties of alumina membrane are affected by many factors, including the kind of electrolyte, current density, power on time, temperature, additive and so on. Glycerol was added as an additive, which can not only increase the thickness of alumina membrane, but also enhancing the toughness of alumina membrane. This paper discusses the influence of glycerol addition on the anodic oxidation of aluminium, based on other factors under the condition of optimal value. We Select the high pure aluminum as anode and lead net as the cathode, putting them in sulfuric acid solution for anodizing. At last, we test the colour effect, corrosion resistance and thickness of the alumina membrane. It turns out that adding a certain amount of glycerol can enhance the properties of alumina membrane, but adding more can reduce the properties of it. Keywords ： alumina membrane anodic oxidation organic additive glycerol 1 研究进展 铝对氧具有较强的化学亲和力，表面极易生成一层极薄的氧化膜， 起到一定的防护作用。但该层氧化膜孔隙率大，机械强度低,抗蚀和耐 磨性都不能满足防腐蚀要求，从而真正地保护铝基体。 随着铝制品工业的不断完善发展,人们开始采用各种方法以达到 工艺上的要求, 阳极氧化法就是其中最为常用的一种。阳极氧化法为 电化学方法。利用此法可 铝（或铝合金）的表面生成致密的优质氧化 膜，其厚度可达几十至几百微米，有效提高铝的耐腐蚀性。此外，所形 成的的氧化膜存在均匀的孔隙，可用有机染料进行染色处理，经封闭 后色泽稳定，使铝材应用更加广泛。根据氧化膜的用途也在阳极氧化 的同时，进行其它工艺得到相应的氧化膜。 铝的阳极氧化工艺最早出现 20 世纪20年代，50年代已广泛使 用