英文版新造船涂装工艺.docxVIP

Painting procedure General All steel to build this vessel should be coated with inorganic zinc shop primer prior to being used . The application work to be performed in accordance with the builder’s practice and the paint manufacturer’s recommendation, application should be preformed under the guidance of on-site technical representative. The colors of final paint are to be in accordance with owner’s standard. The color of each coat except final paint is to be decided by the builder in consideration of manufacturer’s color card. The position or area which are not specified in the scheme of paint of this specification shall be applied same as the surroundings. Executive standard: ISO 08501-1 :1988 steel surface rust grade and surface preparation grades before paint application. CB/Z227 -86 coating film thickness measuring means Primary preparation all steel plates used for the construction of the vessel and with thickness same or more than 6 mm are to be shot blasted by automatic line to ISO 8501 -1:1988 Sa2.5（hereinafter all mentioned de-rusting grades are according to ISO Standard）,after blasting, the surface profile (RZ) should be between 35-85 microns, equals, to the profile of ISO8503 Medium Grade to Course . Grit or blasting to Sa2.5 or power tools grit to St3 may be applied instead of shot blasting is considered impractical. After surface preparation, all steel material must be protected by one coat of inorganic zinc silicate shop primer with DFT (Dry Film Thickness) of 15-25 microns. Different color shop primer to be used for mild ad high tensile steel plates and sections all steel plates and sections can not be used for vessel if no managed Second preparation 1. Before block sandblasting, port of all pipe that are installed should be wrapped with protective material to avoid incursion by dust. The galvanized pipe in various water tanks should be protected to avoid damaging the galvanized film during de- rusting. for secondary preparation, grinding or blast