煤焦油管道腐蚀原因的探讨及应对措施_索振华.pdfVIP

·100 · 内燃机与配件 煤焦油管道腐蚀原因的探讨及应对措施 索振华 河北邢矿硅业科技有限公司，邢台055150） （ 摘要：本文主要分析了煤焦油管道腐蚀发生的机理及防治措施。煤焦油管道腐蚀的原因主要有氯离子导致的点蚀、溶解氧引发的 腐蚀、高速流体和游离碳造成的腐蚀、湿硫化氢引发的腐蚀、微生物引发的腐蚀，固定铵盐引发的腐蚀等。针对以上原因，可以采取加 入钠盐、焦油静置脱水、焦油除渣、改进蒸馏工艺等防治措施。 Abstract: This paper analyzes the mechanism of coal tar pipeline corrosion and control measures. The main reasons of coal tar pipeline corrosion include pitting caused by chloride, corrosion caused by dissolved oxygen, corrosion caused by high velocity fluid and free carbon, corrosion caused by wet hydrogen sulfide, corrosion caused by microbiology and corrosion caused by fixed ammonium salt. The controlled measures of coal tar pipeline corrosion are: adding sodium salt, dehydration of tar through setting, tar slag, improving distillation process, and so on. 关键词： 焦油；管道；腐蚀 煤 Key words: coal tar ；pipeline ；corrosion DOI:10.19475/j.cnki.issn1674-957x.2017.04.046 0 引言 管道发生局部破裂，造成泄漏，不仅中断了管道的正常运 炼焦工业中煤热解生成的产物非常复杂，目前煤焦油 输，而且还会造成环境污染，甚至可能引起灾难性事故。据 管道中查明的产物有500 多种，其中可以提取出的有200 统计，我国每年因管道腐蚀损失数亿元，因此，了解煤焦油 多种，煤焦油是炼焦工业的重要产物之一，它是一种具有刺 管道腐蚀的原因，寻找有效的防腐措施，延长管道使用时 激性臭味的黑色或者黑褐色粘稠状液体，按照煤干馏温度 间，保证煤焦油管道的畅通，对煤焦油管道的高效利用有 的不同，煤焦油可分为：中低温煤焦油和高温煤焦油。随着 着突破性意义[3，4] 。 炼焦企业的快速发展，以及国际市场对焦炭需求量的增加， 1 煤焦油管道腐蚀的成因及分析 2010 年我国煤焦油产量达1400 万吨，它可用来生产塑料、 煤焦油成分复杂，主要有苯类、酚类、含氮化合物、含 合成纤维、染料、橡胶、医药、耐温高材料等有机产品，也可 硫化合物、水、盐类及煤粉、焦粒、金属化合物。在煤焦油管 以用来合成杀虫剂、糖精、染料、药品、炸药等工业品[1]。 道中发生的腐蚀情况分为：冲击腐蚀、晶间腐蚀和电化学 煤焦油化学发展至今将近200 年历史。从1822 年英 腐蚀。冲击腐蚀是指流体冲击和腐蚀的联合作用而引起的 国建立起世界上第一个煤焦油蒸馏工厂，直到19 世纪后 材料损伤，例如：高速流体造成的腐蚀；晶间腐蚀是指金属 半期，英国和德国相继开发煤焦油下游产品，从此奠定了 材料的晶粒与其内部间的晶界杂质的存在造成的腐蚀，例 现代有机化学工业的基础。 如：氯离子导致的点蚀；电化学腐蚀是指金属不纯的材料 在我国，煤焦油产业已趋向于成熟，但煤焦油管道腐