WELDING PROCEDURE SPECIFICATION(WPS)
(In accordance with AWS D1.1/D1.1M:2020)
Company Name:
Project Name:
Client:
Authorized by:
Welding Process(es) :
WPS No. :
Rev. No.:
Date:
Supporting PQR No.(s) :
BASE METALS
Specification
Type or Grade
AWS Group No.
Base Material
ASTM A572
50
Ⅱ
Welded To
ASTM A572
50
Ⅱ
Backing Material
ASTM A572
50
Ⅱ
Other
None
POSTWELD HEAT TREATMENT
Temperature
-
Time at Temperature
-
Other
None
BASE METAL THICKNESS
As-Welded
With PWHT
CJP Groove Welds
12
-
CJP Groove w/CVN
-
-
PJP Groove Welds
-
-
Fillet Welds
Unlimited
-
DIAMETER直径
-
-
JOINT DETAILS
Groove Type
See the Sketch
Groove Angle
See the Sketch
Root Opening
6
Root Face
N/A
Backgouging
-
Method
N/A
JOINTS DETAILS(Sketch)
w:backing width shall be 75mm min. when not removed for RT,otherwise 25 mm min.。
PROCEDURE
Weld Layer(s)
All
Weld Pass(es)
All
Process焊接方法
FCAW
Type(Semiautomatic,Mechanized,etc.)
Semiautomatic
Position
F
Vertical Progression
-
Filler Metal(AWS Spec.)
A5.20
AWS Classification
E71T-1C
Diameter
Φ1.2
Manufacturer/Trade Name
-
Shielding Gas Compos.(Composition)
99.8%CO2
Flow Rate
20-25L/min
Nozzle Size
I.D.=19mm
Preheat Temperature
Min.10℃
Interpass Temperature
60-250℃
Electrical Characteristics
-
Current Type Polarity
DCEP
Transfer Mode
-
Power Source Type(cc,cv,etc)
cv
Amps
110-350
Volts
18-24
Wire Feed Speed
50-70cm/min
Travel Speed
20-30cm/min
Maximum Heat Input
25.2KJ/cm
Technique
-
Stringer or Weave
Stringer
Multi or Single Pass(per side)
Multipass
Oscillation(Mechanized/Automatic)
-
Traverse Length
-
Traverse Speed
-
Dwell Time
-
Number of Electrodes
1
Contact Tube to Work Distance
-
Peening
None
Interpass Cleaning
Brushing
Other
None
Prepared by _________________________________ Date
Reviewed By _________________________________ Date
Approved by Date