水利工程混凝土施工质量通病防治.pdfVIP

水利工程混凝土施工质量通病及防治 摘要：随着社会的发展，水利工程建设中混凝土的使用率越来越高，是水利工程建设中的重要材料。但 在混凝土工程施工过程中，由于配合比、原材料、操作工艺、技术等原因，使混凝土结构物产生一些质 量问题，如裂缝、气泡、麻面、露筋、蜂窝孔洞等。本文分析了水利工程中混凝土质量通病形成的原 因，找出解决办法，对工程进行有效预控。 关键词：水利工程 混凝土质量通病防治 abstract: with the development of society, the water conservancy project construction of concrete utilization rate is higher and higher, in the construction of water project is an important material. but in the concrete construction process, because of raw materials, mixing ratio, operation process, technology and other reasons, make concrete structures produce some quality problems, such as crack, bubble, pits and dew muscle, the honeycomb holes, etc. this paper analyzes the concrete in water conservancy project the causes of the formation of the common faults, and find out the solution for engineering for effective control counter. keywords: water conservancy project concrete prevention and control of quality problems 中图分类号：u449.7 文献标识码：a文章编号： 随着我国经济的不断增长，水利建设工程也发展迅速。混凝土因其抗压强度高，取材广泛，可塑性性 强，并且不易风化，耐火性好，养护费用低等，成为当今水利建筑中使用最广泛的材料之一。由于在施 工混凝土浇筑过程中容易遇到各种问题，以及因其自身情况，硬化成型的混凝土中容易存在着气穴、微 孔隙和微小裂缝，这些裂缝的存在降低了钢筋混凝土材料的抗渗能力、承载能力和耐久性。本文针对水 工建筑混凝土结构通病的成因进行分析，并提出防治技术。 1.裂缝 （1）裂缝形成的原因 裂缝较常见的形成原因是砂石、水泥等质量不好。如果水泥受潮、强度不够或超期，导致混凝土强度达 不到设计值，就可能使混凝土产生裂缝。要想工程质量从根本上得到保证，就必须把好材料的质量关。 混凝土的抗拉强度直接受混凝土配合比的影响，配合比不当，是造成其开裂不可忽视的原因。配合比不 当是指水灰比大，水泥用量过大，含砂率不当，选用外加剂不当，骨料种类不佳等，这几个因素是互相 关联的。施工原因造成混凝土开裂的因素有很多，水分蒸发、混凝土干缩和水泥结石通常是导致混凝土 开裂的重要原因。模板构造不当、支撑刚度不足、漏浆、过拆模、支撑地基下沉等都有可能造成混凝土 开裂。因此混凝土的搅拌、运输、浇灌、振实各道工序中的任何疏漏和缺陷，都会直接或间接使混凝土 产生裂缝。 （2）预防混凝土裂缝的具体措施 优化设计配合比。选择减水剂，掺入粉煤灰，保证泵送的流动度。试拌原材料，添加i级粉煤灰，尽可能 地减少水泥用量，在规范允许的范围内控制水灰比，粗骨料采用二级配。粉煤灰的适量掺入对降低温 升，改善混凝土的和易性，提高抗侵蚀，减少收缩具有良好的作用。 原材料的选择。碎石针片状控制在10%以内，含泥量控制在1%内，砂料的细度模数控制在2.4以上，含泥 量控制在1%内。尽可能使用低水热化水泥，控制原材料的质量，不使混凝土产生收缩。 施工安排。混凝土的浇筑尽可能避开曝晒、高温、降温、多风的天气，若必须在上述条件下施工时，须 有相应遮挡、保温措施。 施工过程控制。混凝土沉缩裂缝可通过二次振捣法消除。进行二次振捣可以使坍落度已经消失、开始初 凝的混凝土重新液化，能较好地消除钢筋下面、粗骨料的水膜，消除沉缩收缩量。泵送混凝土尤其需要 二次振捣。在混凝土终凝前再进行二次入工抹压收光。 混凝土干缩裂缝的控制措施。混凝土中若存在空隙则产生湿胀干缩，消除方法是加强振捣强度，清除混 凝土中