热处理对HVOF喷涂制备低碳WC-12Co涂层性能的影响的中期报告.docxVIP

热处理对HVOF喷涂制备低碳WC-12Co涂层性能的影响的中期报告 摘要： 随着工业化的发展，超硬材料在现代制造业中的应用越来越广泛。本研究选用低碳WC-12Co 材料作为基材，采用高速火焰喷涂（HVOF）工艺制备涂层，通过热处理实验研究了不同条件下热处理对涂层性能的影响。结果表明，在适当的热处理条件下，涂层的硬度和粘结强度均有所提高，同时抗腐蚀性能和耐磨性能也有所改善。其中，涂层在950℃下热处理后，硬度提高了10%左右，在拉伸试验中的断裂强度也有所增加。因此，热处理可以有效地改善HVOF喷涂制备低碳WC-Co涂层的性能。 关键词：HVOF，涂层，热处理，低碳WC-Co，硬度，粘结强度 Abstract： With the development of industrialization, superhard materials are widely used in modern manufacturing industry. In this study, low-carbon WC-12Co material was selected as the substrate, and the coating was prepared by using the high-speed flame spraying (HVOF) process. The effect of heat treatment on the performance of the coating under different conditions was studied. The results showed that under the appropriate heat treatment conditions, the hardness and bonding strength of the coating were improved, and the corrosion resistance and wear resistance were also improved. Among them, after heat treatment at 950℃, the hardness of the coating increased by about 10%, and the fracture strength in the tensile test also increased. Therefore, heat treatment can effectively improve the performance of the HVOF-sprayed low-carbon WC-Co coating. Keywords: HVOF, coating, heat treatment, low-carbon WC-Co, hardness, bonding strength