过渡金属掺杂ZnO薄膜的制备及其性能研究的中期报告.docxVIP

过渡金属掺杂ZnO薄膜的制备及其性能研究的中期报告 【摘要】 本文以过渡金属Co为掺杂物，通过溶液法在玻璃基板上制备了Co掺杂的ZnO薄膜。采用X射线衍射仪（XRD）、扫描电子显微镜（SEM）和紫外-可见分光光度计（UV-Vis）等分析手段对样品的物理性质进行了表征。结果表明，制备得到的薄膜为六方晶系，具有良好的晶格匹配性。SEM表明薄膜表面均匀致密，没有明显的裂纹和孔洞。通过UV-Vis测试，发现Co掺杂能够显著提高ZnO薄膜的吸收率，同时可以被用作光催化分解甲醛等有机污染物的催化剂。本研究为探究过渡金属掺杂ZnO材料的制备和应用提供了重要的基础。 【关键词】 过渡金属，掺杂，ZnO薄膜，溶液法，物理性质 【Abstract】 In this paper, Co-doped ZnO thin films were prepared on glass substrates by solution method using transition metal Co as a dopant. The physical properties of the samples were characterized by X-ray diffractometer (XRD), scanning electron microscope (SEM) and ultraviolet-visible spectrophotometer (UV-Vis). The results show that the prepared film has a hexagonal crystal structure with good lattice matching. SEM shows that the film surface is uniform and dense, without obvious cracks and pores. Through UV-Vis testing, it was found that Co doping can significantly increase the absorption rate of ZnO thin film, and can be used as a catalyst for the photocatalytic decomposition of organic pollutants such as formaldehyde. This study provides an important foundation for exploring the preparation and application of transition metal-doped ZnO materials. 【Keywords】Transition metal, doping, ZnO thin film, solution method, physical properties.