热膨胀法测量陶瓷烧成温度模拟实验研究.pdfVIP

热膨胀法测量陶瓷烧成温度模拟试验争论

汪常明;童永东

【摘要】热膨胀法古陶瓷测温中升温速率、烧结程度、推断曲线的选择、分析方

法等因素会影响测温精度.为提高测温精度,通过不同升温速率对各种具有烧成温度

模拟样品的测温试验,建立了一套热膨胀法古陶瓷测温的参考程序.此外,依据测量值

与实际烧成温度之间的定量关系,利用线性拟合的方法推算出了用于减小测温误差

的校正公式.试验结果显示:校正公式在指定的温度范围内可大幅提高测温精度

.%Heatingrate,sinteringextent,judgmentcurveselection,analysis

methodarefactorswhichaffectthetemperaturemeasurementaccuracyin

determinationofthefiringtemperaturebythermalexpansion

measurement.Toimprovethetemperaturemeasurementaccuracy,

throughtemperaturemeasuringexperimentforsomekindsofsimu-lated

sampleswithknownsinteringtemperatureunderdifferentheatingrates,a

standardofapplicationmethodhasbeenestablished.Inaddition,

accordingtothequantitativerelationshipbetweenmeasuredvalueand

theactualfir-ingtemperature,acorrectionformulausedtoreducethe

temperaturemeasurementerrorwasderivedbylinearfittingmethod.The

experimentresultsshowthatthecorrectionformulacansignificantly

improvethetemperaturemeasuringaccuracyatthespecifiedtemperature

range.

【期刊名称】《科学技术与工程》

【年(卷),期】2023(018)016

【总页数】6页(P86-91)

【关键词】升温速率;热膨胀法;古陶瓷测温

【作者】汪常明;童永东

【作者单位】广西民族大学科技考古试验室,南宁530006;美国亚利桑那大学人类

学学院,图森85721;广西民族大学科技考古试验室,南宁530006

【正文语种】中文

【中图分类】O59

对于古陶瓷的争论，烧成温度是至关重要的，由于它是古代陶瓷制作技术力气，高

温技术水平以及窑性能的重要表达。除在考古学上的直接意义外，烧成温度还为争

论和复原古陶瓷器烧制工艺供给关键信息。另外，烧成温度还对古陶瓷和窑的其他

科学争论(如热释光和地磁测年)有重要价值[1]。因此，烧成温度的测定对于古陶瓷

争论有格外重要的意义。

20世纪50年月末Terrisse首次将热膨胀法真正意义上引入古陶瓷测温[2]，60年月

Tite[1]提出了该方法基于的理论假设。中国20世纪50年月末周仁、李家治[3，4]

最早将热膨仪应用到古陶瓷的测温中。文献[5—8]先后争论了热膨胀法应用于低温

陶器逐步升温屡次重烧的测温方法。李迎华等[9—11]较系统地争论了热膨胀法

古陶瓷测温。

热膨胀法在具体测温过程中仍有很多问题值得深入争论，比方前人工作没有综合考

虑古陶瓷的烧结程度，材料类型，在测试过程中的升温速率，推断曲线的选择，起

始点确定，样品尺寸等这些因素对测温结果带来的影响；测温时的具体操作方法和

分析方法也未在大量模拟试验根底之上建立一个合理的参考标准，致使测温操作因

人而异，结果存在明显的人为误差；对于热膨胀法古陶瓷测温的理论争论也不够深

入。以上这些问题都会对热膨胀法在古陶瓷测温中的牢靠性和准确性带来或大或小

的影响，因此对该方法的进一步争论势在必行。

现旨在考虑烧结程度、升温速率、推断曲线选择，起始点确定等因素不同状况下通

过大量模拟试验为热膨胀法古陶瓷测温建立一套适宜的参考程序。

由于热膨胀法古陶瓷测温的常规方法不适用于原始烧成温度低于870℃的低