高弹性聚丙烯酰胺水凝胶的制备及拉伸性能研究 .pdfVIP

高弹性聚丙烯酰胺水凝胶的制备及拉伸性能研究

肖新才;张瑞连;熊小翠;胡蓉蓉;马文婷

【摘要】为了提高水凝胶的弹性性能,采用微凝胶法制备了高弹性的聚丙烯酰胺

(PAAM)水凝胶.先采用沉降聚合法制备了PAAM微凝胶,再以此充当交联剂代替传

统的化学交联剂和引发剂,制备了高机械性能的PAAM水凝胶.同时探讨了丙烯酰胺

浓度、凝胶成型温度、微凝胶与水的体积比对PAAM水凝胶弹性性能的影响.结果

表明:随着丙烯酰胺的浓度的增大,凝胶柱的弹性模量变大;随微凝胶成型温度越高,形

成的水凝胶的弹性模量越小;当微凝胶与水的体积比为1∶1时,水凝胶的弹性模量

较大,增加或减少微凝胶的量均会使得水凝胶的弹性模量变小.%Toimprovethe

elasticityofthehydrogels,microgelmethodwasappliedtopreparehighly

elasticpolyacrylamide(PAAM)hydrogel.PAAMmicrogelswerepreparedby

sedimentationpolymerization,thenhighlyelasticPAAMhydrogelwas

preparedusingthemicrogelsasthecrosslinkerinsteadofthetraditional

chemicalcrosslinkerandinitiator.Theeffectsofacrylamideconcentration,

polymerizationtemperature,volumeratioofthemicrogelsandwateron

theelasticityofthehydrogelswereinvestigated.Theresultsindicatedthat

theelasticitymodulusofPAAMhydrogelincreasedwiththeincreaseof

acrylamideconcentrationanddecreasedwiththepolymerization

temperature.Themoduluswaslargestwhenthevolumeratioofthe

microgelsandwaterwas1∶1,whichwoulddecreaseregardlessof

decreasingorincreasingthemicrogelscontent.

【期刊名称】《中南民族大学学报（自然科学版）》

【年(卷),期】2017(036)001

【总页数】5页(P47-51)

【关键词】聚丙烯酰胺;微凝胶;高弹性;微凝胶法;弹性模量

【作者】肖新才;张瑞连;熊小翠;胡蓉蓉;马文婷

【作者单位】中南民族大学药学院,武汉430074;中南民族大学药学院,武汉

430074;中南民族大学药学院,武汉430074;中南民族大学药学院,武汉430074;中

南民族大学药学院,武汉430074

【正文语种】中文

【中图分类】TQ460.1;R944.1

聚丙烯酰胺(PAAM)具有典型的三维网络结构、无毒副作用、性能稳定，被广泛应

用于生物水凝胶的制备[1]，如蛋白质分离[2,3]、药物释放[4,5]、土壤改良剂[6]等.

由于PAAM水凝胶的机械强度较低，使其在强度要求相对较高的领域，如人工肌

肉骨骼、记忆开关元件、机械传动装置及生物传感器等的应用受到很大的限制.传

统的提高水凝胶机械强度的方法有增加交联密度、降低凝胶溶胀度、引入纤维状增

强剂、制备互穿网络(IPN)等[7]，但操作较繁琐，或对水凝胶的机械性能的改善能

力有限，或改变了PAAM其本身的性能，使PAAM水凝胶应用受限.

传统的凝胶以N,N-亚甲基双丙烯酰胺为化学交联剂来制备.近年来，诸多研究者按

此模式，通过构建聚合物的交联来改变水凝胶的机械强度，如构建拓扑结构[8]、

双网络结构[9-11]、复合结构[12]，及加入纳米凝胶作为交联剂制备水凝胶[13-15]

等.利用活性纳米粒子如锂皂石[15]、氧化石墨烯[16]、离子[17]、二氧化