P123模板剂用量对超细镍钼加氢催化剂结构及性能的影响

熊良军;李为民;朱毅青;兰永平

【摘要】WithtriblockcopolymerP123astemplate,fourNi-Mo/TiO2-SiO2

catalystprecursorswithdifferentP123additiveamount(n(P123)/n(Ti+Si))

werepreparedbysol-gelmethod.Thephysicalpropertiesofthefour

catalystswerecharacterizedbyTG-DTA,N2adsorption-desorption,XRD,

H2-TPRandHRTEM.Inthecontinuousfixedbedreactor,the

hydrodearomatizationactivitiesofthefourcatalystswereevaluatedwith

200#low-sulphurcontentkeroseneasrawmaterial.Theresultsshowed

thattheadditionofP123affectedgrainsizeofactivecomponentandpore

structureofcatalystobviously.Theactivecomponentswereuniformly

distributedandwithoutevidentappearanceofaggregationoncatalyst,

andgraindiametersofthefourcatalystswerebetween4-5nm.

Appropriatespecificsurfaceareaandporedistributionofthecatalystwere

profitabletohydrodearomatizationofkerosene.Afterprocess

optimization,overtheNi-Mo/TiO2-SiO2catalystwithn(P123)/n(Ti+Si)=0.

005,massfractionofalkylbenzeneinkerosenewasreducedto0.41%and

massfractionofnaphthaleneinkerosenedecreasedto280μg/g,andthe

aromaticsrejectionratereached95.98%,whichmettheproductstandard

ofJLD-40forhydrodearomatizationsolventoil.%以三嵌段共聚物P123为模

板剂,采用溶胶-凝胶法制得不同P123用量(以n(P123)/n(Ti+Si)计)的Ni-

Mo/TiO2-SiO2催化剂前躯体；采用TG-DTA、N2吸附-脱附、XRD、H2-TPR

和HRTEM对催化剂进行表征；在固定床连续流动微反装置上,以200#低硫煤油

为原料,考察催化剂的加氢脱芳烃性能.结果表明,P123用量对催化剂活性组分晶粒

尺寸和孔结构参数有明显的影响；催化剂的活性组分分布均匀,没有明显的团聚现

象,粒径在4～5nm；催化剂适宜的比表面积和孔结构有利于煤油的加氢脱芳烃；

经过工艺优化,采用P123模板剂的Ni-Mo/TiO2-SiO2系列催化剂

中,n(P123)/n(Ti+Si)为0.005的催化剂能将煤油中的烷基苯质量分数降至0.41％,

萘质量分数降至280μg/g,芳烃脱除率达到95.98％,产品的芳烃含量达到JLD-40

脱芳烃溶剂油的产品标准要求.