2A16铝合金中应变率力学性能研究

惠旭龙;白春玉;葛宇静;舒挽

【摘要】Inordertostudythedynamicpropertiesof2A16aluminumalloy

andtheinfluenceofheattreatmentonitsstrainratesensitivity

property,testson2A16aluminumalloy(heat-treatedconditionOandT4)

underquasi-staticandintermediatestrainratewereperformedbyusing

anelectronicuniversaltestingmachineandahighvelocityhydraulicservo-

testingmachineatroomtemperature.Thestress-straincurvesunder

differentstrainrateswereobtained,andamodifiedJohnson-Cook

constitutivemodelwasfitted.Theresultsshowthattheheat-treated

conditionhasabiginfluenceonthestrainratesensitivitypropertyof2A16

aluminumalloyunderthestrainratebetween10-4～102s-1,andthe

strainratehardeningeffectof2A16-Oaluminumalloyisobvious,butthat

of2A16-T4aluminumalloyisnotsoevident.Inaddition,thestrain

hardeningeffectisobviousforbothofthematerialsunderthestrainrate

between104～102s-1Moreover,themodifiedJohnson-Cook

constitutivemodelcanpredictthetestresultsverywell.%为研究2A16铝合

金的中应变率力学性能及热处理状态对其应变率敏感性的影响,利用电子万能试验

机和高速液压伺服试验机对其(O状态和T4状态)进行常温下准静态和中应变率力

学性能试验,得到不同应变率下的应力应变曲线,并基于修正的Johnson-Cook本构

模型对其进行拟合.结果表明:在应变率10-4～102s-1内,热处理状态对2A16铝合

金的应变率敏感性有较大影响,其中2A16-O状态铝合金的应变率敏感性较强,而

2A16-T4状态铝合金的应变率敏感性较弱,但两种材料均具有较强的应变硬化效应;

2A16铝合金中应变率力学性能研究--第1页

2A16铝合金中应变率力学性能研究--第2页

此外,修正Johnson-Cook本构模型的拟合结果与试验结果吻合很好,能够很好表征

材料的动态力学行为.

【期刊名称】《振动与冲击》

【年(卷),期】2017(036)019

【总页数】5页(P66-70)

【关键词】2A16铝合金;热处理状态;中应变率;应变率效应;Johnson-Cook模型