GMW15170-2018-经感应淬火处理的自挤自攻螺钉的材料和性能要求-chs.pdfVIP

MaterialandPerformanceRequirementsforGMW15170

InductionHardenedTypeTR(Thread

共11页第1页

Rolling)TappingScrews

经感应淬火处理的自挤自攻螺钉的材料和性能要求通用标准

Scope范围

ThisstandardcoversmaterialandperformancerequirementsapplicabletoTypeTR(threadrolling)tapping

screws,

heattreatedtoachievepropertiescomparabletopropertyclass10.9screwswithinductionhardenedpoints,

insizes5mmandlarger.

这个标准涵盖材料和性能需求适用于类型TR(搓丝)自攻螺丝,热处理达到性能等级10.9螺丝有感应淬硬区,规格大于

等于5毫米。

1.1MaterialDescription.

1.1.1MaterialIdentification.Whenselectingthelengthofscrewforanyapplication,itshouldbeanobjectiveto

locate

theinductionhardenedzonebeyondtheexitsideofthematingcomponentasdepictedinFigure1,ortomaintaina

minimumlengthofthreadengagementequaltofourfullformnon-inductionhardenedthreadsasillustratedin

Figure

2.Theperformancevaluesspecifiedinthisstandardarenotvalidfordesignuseunlessallconditionsofthe

applicationareidenticaltothecombinationoflaboratoryconditionsdescribedinthetestingprocedure.

1.2Symbols.Notapplicable.

1.3Applications.Thescrewscoveredbythisspecificationaresuitableforuseingeneralengineering

andstructuralattachments.

1.1材料描述。

1.1.1材料标识。在选择对于任何应用螺丝的长度,它应该有一个目标，定位感应淬火区域超出了出口侧的配合部件，

如

图1所示。所示,或保持最小接触螺纹啮合长度等于四个完整的非感应变硬螺纹，如图2所示。

在本标准中规定的性能值对设计使用无效，除非应用的所有条件与测试过程中描述的实验室条件相一致。

1.2符号。不适用。

1.3应用。本规范所涵盖的螺丝适用于一般工程和结构附件。

1.4注:典型的涂层和电镀后的固化和氢脆烘烤通常发生在200℃到350℃之间，可能会导致感应硬化发生软化。

确保成品螺丝满足机械和硬度要求本规范是紧固件制造商的责任。

2References参考文献

Note:Onlythelatestapprovedstandardsareapplicableunlessotherwisespecified.

注:除非另有说明，否则只适用最新批准的标准。

2.1ExternalStandards/Specifications.外部标准/规范

SAEJ423ISO