某锅炉中温再热器连续泄漏原因分析

张宗莹，许志海，杨景建，陈鹏？

摘要：对某电厂1025t/h锅炉中温再热器夹持管泄漏的对接焊缝进行宏观检验、材质成分分析、金相组织检验及

能谱电镜分析。分析认为，异种钢对接焊缝因材质错用承受高应力及低周疲劳应力，而且焊缝根部成形差，局部尺寸突

变造成管段局部超温而形成脱碳区及晶间裂纹。晶间裂纹在焊缝根部熔合线处萌生，向外壁扩展，最终形成穿透型裂纹

导致泄漏。

关键词：材质错用；异种钢对接焊缝；应力腐蚀；晶间裂纹

D0I:10.14158/ki.1001-3814

中图分类号：TG441.7文献标识码：A文章编号：1001-3814(2022)21-0152-04

CauseAnalysisofContinuousLeakageofABoiler

MediumTemperatureReheater

ZHANGZongying,XUZhihai²,YANGJingjian’,CHENPeng?

(1.GansuHengshengPowerConstruction(Group)Co.,Ltd.,Lanzhou730050,China;2.EnergyConstructionGroup

TechnologyDevelopmentCo.,Ltd.,Tianjin300012,China)

Abstract:Theweldingseamoftheholdingpipeofthemediumtemperaturereheaterofa1025t/hboilerinapowerplant

wasanalyzedbymacroscopicinspection,materialcompositionanalysis,metallographicexaminationandenergyspectrum

electronmicroscopeanalysis.Itisconcludedthat,duetomaterialmisapplication,thedissimilarsteelbuttweldbearshigh

stressandlowcyclefatiguestress,andtheweldroothaspoorforming,thedimensionhaslocalsuddenchange,whichcasues

localover-temperatureofthepipesectiontoformdecarbonizationzoneandintercrystallinecracks.Theintercrystallinecracks

initiateatthefusionlineoftheweldrootandexpandtotheouterwall,eventuallyformsthepenetratingcrack,resultingin

leakage.

Keywords:materialmisuse;dissimilarsteelbuttweld;stresscorrosion;intercrystallinecrack

随着电站锅炉向着更大容量、更高蒸汽参数的处理与运行过程中发生合金元素的稀释、碳迁移、残

方向发展，耐热钢与奥氏体不锈钢的异种钢焊接接余应力、蠕变强度的不匹配等，使接头在运行过程中

头在电站锅炉管道连接中得到广泛的应用。国外实早期失效，成为一个突出的问题。具体原因有超温蠕

践表明，异种钢焊接接头在高温高压运行工况下，在变断裂、管材选用不当、异种钢接头存在过大的热应

设计寿命内容易发生早期失效。据统计，该类接头力、焊缝界面有碳迁移过渡层、应