支撑座成形过程数值模拟及工艺优化.pdfVIP

《热加工工艺》2020年3月第49卷第5期

支撑座成形过程数值模拟及工艺优化

陈康,曹建国,黄斯韬,孙阳

(四川大学机械工程学院,四川成都610065)

摘要：对支撑座锻造过程进行了模拟分析，得到了锻件充填不足的原因，即预锻件形状不合理导致锻件局部补料

路径过长。根据锻件缺陷分析结果，优化了锻造工艺，修改了预锻件的形状。通过实际生产获得了质量良好的锻件,锻件

不合格率由32.4%降至14.6%，同时模具寿命得到相应的提升。

关键词：支撑座；充填不足；热锻；模具磨损

DOI:10.14158/j.cnki.1001-3814.

中图分类号：文献标识码：文章编号：

TG316A1001-3814(2020)05-0097-03

NumericalSimulationandTechnologyOptimizationofFormingProcess

forSupportingPedestals

CHENKang,CAOJianguo,HUANGSitao,SUNYang

(SchoolofMechanicalEngineering,SichuanUniversity,Chengdu610065,China)

：

AbstractTheforgingprocessofasupportpedestalwassimulatedandanalyzed,andthereasonofinsufficientfillingof

theforgingwasobtained,thatis,theunreasonableshapeofpre-forgingleadstotoolonglocalfillingpathofforgings.

Accordingtotheanalysisresultsofforgingdefects,theforgingprocesswasoptimizedandtheshapeofpre-forgingwas

modified.Goodqualityforgingswereobtainedthroughactualproduction.Theunqualifiedrateofforgingswasreducedfrom

32.4%to14.6%,andthedielifewasimprovedaccordingly.

Keywords：supportingpedestal;insufficientfilling;hotforging;diewear