热处理对Inconel合金组织的影响.docxVIP

热处理对Inconel690合金组织的影响

宋云京邓化凌

山东电力研究院,山东济南25002；

EffectofHeatTreatmentonmicrostructureofInconel690

SONGYun-jingDENGHua-ling

ShandongElectricPowerResearchInstitute,ShandongJinan250002

ABSTRACT:Theeffectofsolid-solutionandthermaltreatmentonmicrostructure,grainsizeandprecipitatebehaviorwerestudiedinthispaper.Itwasshownthatthesolid-solutiontemperaturehadobviouseffectonthegrainsizeintheInconel690.Thegrainsizeincreasedremarkablywhenthesolutiontemperaturewasover1150℃.Cr23C6precipitatedmainlyinthegrainboundaries.Withtheincreaseofthermaltreatmenttemperatureandtime,theamountandsizeofCr23C6increased.Atthesametime,ThedistributionofCr23C6changedfromdiscretestructuretosemi-continuousstructure.Afterthermaltreatmentof800℃×48h,thesizeofCr23C

KEYWORD:Inconel690;heattreatment;microstructure

摘要：研究固溶和特殊热处理TT处理对Inconel690合金组织的影响,结果表明：固溶温度对Inconel690晶粒度影响较大,温度超过1150℃时,晶粒显着长大,固溶处理应在1100℃以下;TT处理后Cr23C6沿晶界析出,随TT处理温度的增加和保温时间的延长,Cr23C6

关键词：Inconel690合金热处理组织性能

1引言

Inconel690合金因具有优良的抗应力腐蚀IGSCC和晶间腐蚀IGA等能力而被广泛地应用于国内外压水堆核电站蒸汽发生器换热管材料;为提高Inconel690合金的抗应力腐蚀的能力,该材料的一般热处理为固溶处理+特殊热处理TT处理1~4;有研究3表明,固溶温度的高低影响材料的耐腐蚀性能,在950℃～1150℃之间固溶处理时,随着固溶温度的提高,晶间腐蚀率增大;在较低固溶温度处理时,由于碳的固溶度小,一部分未溶的碳化物在晶界存在,在冷却后的新晶界,碳化物的析出量较少,晶界的铬贫化程度较轻,而较高温度下固溶时,未溶碳化物减少,固溶处理后贫铬相对较重;TT处理的目的是改善晶界碳化物的分布和形貌,提高晶界贫铬区的含铬量1;本文主要研究不同温度固溶处理和TT处理后Inconel690合金的组织、晶粒度及碳化物的析出情况;

样品材料采用真空感应+电渣重熔工艺生产冶炼,经挤压、冷拔、冷轧至φ19.05mm×1.09mm的合金管,其主要化学成分%为：；；；；；；；；；等;

对冷轧后的Inconel690合金管进行不同温度的固溶处理及TT处理,固溶处理分别在950℃、1000℃、1050℃、1100℃、1150℃；保温时间5分钟,水冷;TT处理工艺分别为600℃×12h、700℃×12h、700℃×24h、700℃×48h、700℃×96h、800℃×12h、800℃×24h、800℃×48h,冷却方式为水冷;

Inconel合金管的金相组织检测采用MEF4金相显微镜及LEICA-Q500MC型图像分析仪上进行,微观相结构用H800型透射电镜分析,电压为150KV;

2试验结果与分析

固溶处理对组织的影响

图1为Inconel690合金管经四种固溶处理后的微观组织;

图1不同温度固溶后的Inconel690合金的组织

Fig1MicrostructureofInconel690underdifferentannealingtreatments

a950℃、b1000℃、c1050℃、d1100℃、e1150℃

从图1可以看出,Inconel690合金的组织为奥氏体+少量的碳化物,晶粒内存在大