基于Hertz接触理论的涂层界面应力分析.docVIP

基于Hertz接触理论的涂层界面应力分析 楼小玲1，柴国钟1，鲍雨梅1，郝伟娜1，蒋明安2 1浙江工业大学 机械制造及自动化教育部重点实验室Guo-zhong1, BAO Yu-mei1, HAO Wei-na1，JIANG Ming-an2 (1The?MOE?Key?Laboratory?of?Mechanical?Manufacture?and?Automation,?Zhejiang?University?of?Technology，Hangzhou 310032, China 2Taizhou Vocational Technical College, Taizhou 31700, China) Abstract: Finite element package ANSYS is applied to simulate the stress of coating material with contact loaded. The results of finite element method (FEM) and the solutions of classical Hertz analytical method are compared to prove the accuracy of FEM model. The variations of contact stress and contact width with contact load, under different coating thickness and different Young’s modulus are analyzed. The peak value of interface shear stress on coating/ substrate occurs near the central position, and that of the stress of coating/ substrate occurs exactly at the shape center. When the ratio of coating/ substrate Young’s modulus is between 1 and 2.5, the effects of coating/ substrate combination is perfect. The less thickness of the coating may result in the higher interface shear stress and destroy the material. Results of this work are helpful for mechanical research and design of coating material. Key words: coating；Hertz contact；stress analysis  0 引 言 随着高新技术的不断发展，对材料性能的要求愈来愈高。先进涂层材料由于其能把金属材料的特点和涂层材料的特点有机地结合起来，具有金属的强度和韧性和涂层耐高温、耐腐蚀等优点[1-2]，近年来在工程技术领域受到了广泛的重视和应用。 对于涂层材料的接触问题，在理论上得到精确解有很大困难，但随着计算机性能的不断发展，数值方法成为求解的主要途径。涂层/基体的结合强度是考察涂层性能的重要指标，而对应力分布及接触宽度情况的分析研究对考察涂层/基体的结合强度有重要  收稿日期：2006-03-23 基金项目：国家自然科学基金；浙江省自然科学基金（Y104279； Y604051） 作者简介：楼小玲（1981-），女，浙江义乌，硕士研究生 的意义。Diaod等[3]用有限元对单层涂层进行计算，提出了涂层/基体界面不发生屈服的最大接触压力公式，Njiwark等[4]用边界元法计算了单涂层体系的应力场，提出相对膜厚度及弹性模量比是影响表面涂层应力的关键因素。Bouzakis 等[5]、Erkens等[6]采用实验方法分析了接触宽度与载荷的关系。Kagami等[7]研究了当表面粗糙度较高、载荷较小时接触载荷和接触宽度值与Hertz方程计算所得的值不同的原因，分析了粗糙面接触情况下计算接触宽度值比实验值偏小的原由。 笔者主要利用有限元分析软件ANSYS模 拟分析了不同涂层/基体材料匹配及不同涂层厚度下，涂层/基体界面接触应力的分布情况及接触宽度随着载荷的变化情况，为涂层的力学研究及设计提供了一种有效的方法。 1 有限元模型的建立及验证 1.1 Hertz接触基本理论