中型精轧立辊冷却水改造及应用.pdfVIP

2007 中国钢铁年会论文集 中型精轧立辊冷却水改造及应用 王金鹏 孙 斌 张胜利 亓淑红 张富军 （莱芜钢铁股份有限公司型钢厂，莱芜 271104 ） 摘 要 型钢厂中型线轧机由一架可逆式粗轧机和七架连续式精轧机组成，轧辊冷却方式采取冷却水强制冷却 随着产量的逐步提高，生产节奏越来越快，精轧立辊水流量、压力小造成精轧立辊热裂纹较多的问题表现越来越 出，对生产造成了不利影响。为了解决此问题，我们对精轧立辊水冷却水系统进行改造，改善轧辊的冷却条件，进 一步提高轧辊的使用寿命和轧件的表面质量。 关键词 精轧机 轧机立辊 冷却水系统 The Alteration and Application of Stand Roller Cooling Water for Medium Stand Mill Wang Jinpeng Sun Bin Zhang Shengli Qishuhong Zhang Fujun （The Section Steel Plant of Laiwu Iron and Steel Co., Ltd., Laiwu, 271104 ） Abstract Steel wire mill from a medium-reversible roughing mill and seven continuous finishing mill composition, take cooling water cooling roller mandatory cooling. With a gradual increase output, the increasingly rapid pace of production, finishing edger water flow small cracks caused by thermal stress finishing edger showing increasingly more prominent, had an adverse impact on production. To solve this problem, we have to finish edger water. Key words mill, mill roller, cooling water system 1 项目提出的背景 型钢厂中型线轧机由一架可逆式粗轧机和七架连续式精轧机（五架万能轧机和两架轧边机）组成，轧辊 冷却方式采取冷却水强制冷却。冷却水量为 460m3/h ，设计要求水压为 0.4MPa 。其中立辊冷却水流量约 3 80m /h ，实际进轧机前压力只有0.15MPa 。精轧立辊水流量、压力偏小，精轧立辊热裂纹较平辊多。随着产 量的逐步提高，生产节奏越来越快，精轧立辊水流量、压力小的问题表现越来越突出，对生产造成了不利影 响，因此必须对精轧立辊水进行改造。自2005 年以后，随着产量的逐步提高，生产节奏越来越快，精轧立 辊水流量、压力小的问题表现越来越突出，对生产造成了不利影响，主要表现为以下两点：（1）精轧立辊 冷却水压力低，流量小，使轧辊表面温度升高，热裂纹增加，降低了轧辊的使用寿命。自2005 年，我厂立 辊在使用下线后普遍出现了表面热裂纹加重的现象，导致轧辊车削量加大，使用寿命降低，同时引起轧件表 面质量的恶化。统计结果表明，轧辊单次车削量较以往平均增加33% 。（2 ）多次因立辊水流量小，轧辊表 面热裂纹增加，造成换辊，严重时烧坏轧辊，影响生产。 2 原因分析 3 3 精轧立辊水为净化浊环水，原设计流量为80m /h ，供水压力0